E-Fibreglass Welf Triaxial

Identification & Functionality

Chemical Family

Glass Beads & Fibers

Reinforcement Form

Multiaxial Fabric,

Non Crimp Fabrics

Reinforcement Material

Glass Fibers

Composite Materials Functions

Reinforcement

Technologies

Composite Materials

Product Families

Composite Materials — Reinforcements

Glass Fiber

Features & Benefits

Materials Features

Corrosion Resistant,

High Stiffness,

High Strength

Applications & Uses

Markets

Automotive & Transportation,

Building & Construction,

Industrial

Applications

Automotive & Transportation — Automotive

Other Automotive Applications

Building & Construction — Building Materials

Other Building Materials

Industrial — Chemical & Industrial Manufacturing

Other Industrial Applications

Automotive & Transportation — Transportation

Aerospace & Aviation,

Marine

Composites Processing Methods

Hand Lay-up,

Resin Transfer Molding (RTM),

Vacuum Bagging

Properties

Physical Form

Fabric

Technical Details & Test Data

Fabric Specifications

QK0600 - 600 gm Quadriaxial E-Glass
Layer Orientation   degrees (°)	0	+45	90	-45
Layer Weight        (gm/m2)	157	162	132	162
Material	E-Glass	E-Glass	E-Glass	E-Glass

Weight, knitting yarn (gm/m²)	10
Material	PES
Total weight (gm/m²)	623±5%
Standard roll width (mm)	1270

Fabric Specifications

TW0750 - 750gm Weft Triaxial E-Glass
Layer Orientation   degrees (°)	0	+45	90	-45
Layer Weight        (gm/m2)	0	253	248	253
Material		E-Glass	E-Glass	E-Glass

Weight, knitting yarn (gm/m²)			8
Material			PES
Total weight (gm/m²)			762±3%
Standard rol		l width (mm)	1270

Typical Laminate Properties

TYPICAL LAMINATE PROPERTIES Laminate thickness 0.114 per 100gm/m2                                                                                                   Fiber Fraction 50% by weight
	Test Method	0o	+45o	90o	-45o
Tensile Strength	ISO 3268	37* MPa	181 MPa	199 MPa	181 MPa
Tensile Modulus	ISO 3268	9,650 MPa	14,500 MPa	15,860 MPa	14,500 MPa
Compressive Strength	BS 2782	131*MPa	141 MPa	160 MPa	141 MPa
Compressive Modulus	BS 2782	9,900 MPa	13,800 MPa	15,570 MPa	13,800 MPa
Flexural Strength		38* MPa		335 MPa
Shear Strength, in plane	ASTM 4255-83	88 MPa	71 MPa	110 MPa	71 MPa
Shear Strength, interlamina	BS 2782
Elongation at break		2.7%		3.4%

Standard Stock

Order Code			Description	Roll Width	Roll Length
TW0750			750gm Weft Triaxial E-Glass	1.27 m	41.3 Lm
TW750T100			750gm Weft Triaxial E-Glass Tape	100mm	41 Lm
TW750T150			750gm Weft Triaxial E-Glass Tape	150mm	41 Lm
TW750T200			750gm Weft Triaxial E-Glass Tape	200mm	41 Lm

Fabric Specifications

QK0850 - 850 gm Quadriaxial E-Glass
Layer Orientation   degrees (°)	0	+45	90	-45
Layer Weight        (gm/m2)	212	212	212	212
Material	E-Glass	E-Glass	E-Glass	E-Glass

Weight, knitting yarn (gm/m²)	8
Material	PES
Total weight (gm/m²)	856±5%
Standard roll width (mm)	1270

Fabric Specifications

QK1000 - 1000 gm Quadriaxial E-Glass
Layer Orientation   degrees (°)	0	+45	90	-45
Layer Weight        (gm/m2)	236	275	229	275
Material	E-Glass	E-Glass	E-Glass	E-Glass

Weight, knitting yarn (gm/m²)	10
Material	PES
Total weight (gm/m²)	1025±5%
Standard roll width (mm)	1270

Fabric Specifications

QK1200 - 1200 gm Quadriaxial E-Glass
Layer Orientation   degrees (°)	0	+45	90	-45
Layer Weight        (gm/m2)	295	300	300	300
Material	E-Glass	E-Glass	E-Glass	E-Glass

Weight, knitting yarn (gm/m²)	10
Material	PES
Total weight (gm/m²)	1205±5%
Standard roll width (mm)	1270

Standard Stock

Order Code	Description	Roll Width	Roll Length
QK0600	600 gm Quadraxial E/Glass	1.27 m	50.6 Lm
QK0850	850 gm Quadraxial E/Glass	1.27 m	36.8 Lm
QK1000	1000 gm Quadraxial E/Glass	1.27 m	30.8 Lm
QK1200	1200 gm Quadraxial E/Glass	1.27 m	26.1 Lm

Packaging & Availability

Packaging Type

Rolls

Storage & Handling

Storage

• NCF Reinforcements should be stored on packaging roll, and kept dry and clean.