Features & Benefits
- Materials Features
- Performance advantage
Considering that glass fibers have a density of 2600 kg/m3 and a tensile modulus of 70 GPa, the flax ampliTex® 0°/90° 200 gsm can replace a 330 gsm glass fiber 0°/90° fabric to have the same stiffness in tension.
In compression, the performance of flax is a bit lower, thus the flax ampliTex° 0°/90° 200 gsm can replace a 275 gsm glass fiber 0°/90° fabric to have the same stiffness.
Applications & Uses
- Applications
- Compatible Polymers & Resins
- Composites Processing Methods
- Processing guidelines
Great compatibility with epoxy and polyester
Near zero CTE, hence good processing compatibility with carbon fibers
Compatible with infusion based processes (vacuum infusion, RTM), wet layup, bladder inflation molding (BIM) and compression molding Flax fibers always contain some humidity at ambient conditions. Some resins (especially polyesters) are sensitive to moisture and may badly polymerize or create bubbles. In that case, dry the fabrics before use (110°C for 15 minutes)
Fiber weight fraction of 50% can be reached with process pressure > 5 bars. However, the fibers absorb a lot of resin when hand-laminating the fabric and it tends to look "dry" (unless too much resin is used) before pressure is applied. We recommend controlling the amount of adhesive used for laminating and impregnating it with 50 to 60% resin in weight. Excess resin comes out while pressing the fabric.
Properties
- Physical Form
- Mechanical Properties
Value | Units | Test Method / Conditions | |
Tensile Modulus // to fibres | 60.0 | GPa | - |
Tensile Modulus ⊥ to fibres | 6.1 | GPa | - |
Tensile Strength // to fibres | 630.0 | MPa | - |
Flexural Modulus // to fibres | 54.0 | GPa | - |
Flexural Modulus ⊥ to fibres | 6.1 | GPa | - |
Flexural Strength ⊥ to fibres | 692.0 | MPa | - |
Flexural Yield strength // to fibres | 190.0 | MPa | - |
Density | 1350.0 | kg/m3 | - |