Working Life - Will vary according to temperature. At 77°F (25°C), use all mixed material within 13 minutes.
Coverage Rate - Film thickness and coverage rate will vary with porosity and profile of the substrate. Each 6 kg unit will give a practical coverage rate of 205 ft2 (19 m2)
Cure Time - Allow to solidify for the times shown in the Belzona IFU before subjecting it to the conditions indicated.
Volume Capacity
330 in3 (5420 cm3)/ 6 kg unitBase Component
Appearance Clear Liquid Color Light amber Viscosity 5-7 poise at 77°F (25°C)
Density 1.16 g/cm3 Solidifier Component
Appearance Clear Liquid Color Amber Viscosity 0.5-1.5 poise at 77°F (25°C)
Density 1.00 g/cm3 VOC content (ASTM D2369 / EPA ref.24) 2.89% / 32.8 g/L Mixing Ratio
For mixing small quantities the mixing ratio of the components is:
Base : Solidifier
by weight: 2.4:1
by volume: 2:1
Properties
- Typical Properties
- Electrical Properties
Value | Units | Test Method / Conditions | |
Barcol [28 days, 72°F (22°C)] | 77.0 | — | ASTM D2583 |
Barcol [4 hours, 212°F (100°C)] | 81.0 | — | ASTM D2583 |
Barcol [7 days, 72°F (22°C)] | 71.0 | — | ASTM D2583 |
Compressive Strength | 13,000 (89,63) | psi (MPa) | ASTM D695 |
Compressive Yield Strength [28 days, 72°F (22°C)] | 6,600 (45.5) | psi (MPa) | ASTM D695 |
Compressive Yield Strength [4 hours, 212°F (100°C)] | 6,900 (47.6) | psi (MPa) | ASTM D695 |
Compressive Yield Strength [7 days, 72°F (22°C)] | 6,200 (42.7) | psi (MPa) | ASTM D695 |
Damp Quarry Tiles | 450 (3.10) | psi (MPa) | — |
Dielectric Constant | 2.82 | — | ASTM D150 |
Disbondment Diameter (73°F, 23°C) | 0.18 (4.5) | in(mm) | ASTM G8 |
Dry (CS17 wheels) | 72.0 | mm3 | ASTM D4060 |
Dry Concrete | 500 (3.45) | psi (MPa) | — |
Dry Quarry Tiles | 1100 (7.58) | psi (MPa) | — |
Elongation (7 days 72°F[22°C]) | 1.7 | % | ASTM D638 |
Elongation (28 days 72°F[22°C]) | 1.1 | % | ASTM D638 |
Flexural Modulus (28 days, 72°F[22°C]) | 3.4 x 10^5 (2344) | psi (MPa) | ASTM D790 |
Flexural Modulus (4 hours, 212°F[100°C]) | 3.9 x 10^5 (2689) | psi (MPa) | ASTM D790 |
Flexural Modulus (7 days, 72°F[22°C]) | 2.8 x 10^5 (1930) | psi (MPa) | ASTM D790 |
Flexural Strength | 13,000 (89.63) | psi (MPa) | ASTM D790 |
Flexural Strength (28 days, 72°F[22°C]) | 7,190 (49.6) | psi (MPa) | ASTM D790 |
Flexural Strength (4 hours, 212°F[100°C]) | 7,630 (52.6) | psi (MPa) | ASTM D790 |
Flexural Strength (7 days, 72°F[22°C]) | 4,860 (33.5) | psi (MPa) | ASTM D790 |
Hardness (28 days, 72°F[22°C]) | 84.0 | Shore D | ASTM D2240 |
Hardness (4 hours, 212°F[100°C]) | 87.0 | Shore D | ASTM D2240 |
Hardness (7 days, 72°F[22°C]) | 81.0 | Shore D | ASTM D2240 |
Heat Distortion Temperature (HDT) | 106 (41) | °F (°C) | ASTM D648 |
Impact Strength D (28 days, 72°F[22°C]) | 2.66 (5.6) | ft.llb/in2 (KJ/m2) | ASTM D256 |
Impact Strength D (4 hours, 212°F[100°C]) | 2.28 (4.8) | ft.llb/in2 (KJ/m2) | ASTM D256 |
Impact Strength D (7 days, 72°F[22°C]) | 3.71 (7.8) | ft.llb/in2 (KJ/m2) | ASTM D256 |
Koenig Pendulum (28 days, 72°F[22°C]) | 118.0 | seconds | ISO 1522 |
Koenig Pendulum (4 hours, 212°F[100°C]) | 142.0 | seconds | ISO 1522 |
Koenig Pendulum (7 days, 72°F[22°C]) | 107.0 | seconds | ISO 1522 |
Hardness | 82.0 | Shore D | ASTM D2240 |
Tensile Shear Adhesion | 2,700 (18.61) | psi (MPa) | ASTM D1002 |
Tensile Strength | 4,600 (31.71) | psi (MPa) | ASTM D638 |
Tensile Strength Maximum (28 days, 72°F[22°C]) | 4187 (28.87) | psi (MPa) | ASTM D638 |
Tensile Strength Maximum (7 days, 72°F[22°C]) | 3250 (22.41) | psi (MPa) | ASTM D638 |
Tensile Strength Yield (28 days, 72°F[22°C]) | 3261 (22.48) | psi (MPa) | ASTM D638 |
Tensile Strength Yield (7 days, 72°F[22°C]) | 1703 (11.71) | psi (MPa) | ASTM D638 |
Wet (H10 wheels) | 427.0 | mm3 | ASTM D4060 |
Wet Concrete | 475 (3.27) | psi (MPa) | — |
Young’s Modulus (28 days, 72°F[22°C]) | 3.4 x 10^5 (2344) | psi (MPa) | ASTM D638 |
Young’s Modulus (7 days, 72°F[22°C]) | 2.5 x 10^5 (1724) | psi (MPa) | ASTM D638 |
Value | Units | Test Method / Conditions | |
Dielectric Strength (2kV/s) | 48.7 | kV/mm | ASTM D149 |
Surface Resistivity | 4402.0 | Mohm | ASTM D257 |
Regulatory & Compliance
- Certifications & Compliance
Technical Details & Test Data
- Chemical Resistance
Once fully cured, the material will demonstrate excellent resistance to most commonly found inorganic acids and alkalis at concentrations up to 20%. The material is also resistant to hydro-carbons, mineral oils, lubricating oils and many other commonly found chemicals.
- Heat Resistance
Dry Heat Resistance
The indicated degradation temperature in air based on Differential Scanning Calorimetry (DSC) operated in accordance with |SO11357 is typically 320°F (160°C).
For many applications, the product is suitable down to -40°F (-40°C).- Shrinkage
The material, when tested in accordance with ASTM C157, will show no measurable shrinkage during cure.
Storage & Handling
- Shelf Life
Separate base and solidifier components shall have a shelf life of 5 years from date of manufacture when stored in their original unopened containers between 32°F (0°C) and 86°F (30°C).