- XP 24250 is designed to be diluted with polyethylene to a final NuPlastiQ® content between 10% and 40%.
- XP 24250 can be run on existing process equipment with a few adjustments.
- Films made with NuPlastiQ are more sensitive to processing conditions such as temperature profile, residence time, die gap, and blow-up ratio. See the NuPlastiQ Film Processing Guide for additional information.
- A typical recommended temperature profile will be in the 160 °C – 190 °C range.
- Depending on equipment, process conditions, and residence time, as temperatures increase in this range the glycerin plasticizer may experience some volatilization. This may cause a slight odor and/or smoke and is expected under normal processing conditions. Always use proper ventilation. See the BioBlend® XP 24250 SDS for details.
- Some equipment (multi-layer, higher output, lower residence time) may allow for higher processing temperatures (190 °C - 200 °C).
- Melt temperatures above 205 °C may cause material degradation, lensing and fish-eyes in the film.
- When extruder operation has to be stopped temporarily, it is recommended to purge the material in the barrel before resuming film processing.
Applications & Uses
- Applications
- Compatible Polymers & Resins
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
- Applications
- Used for final products requiring strength and plasticity such as agricultural film, blown film, cast film, food packaging, and heavy duty bags.
Properties
- Physical Form
- Mechanical Properties
- Physical Properties
- Typical Properties
- Thermal Properties
- Film Properties
- Flexural Properties
- Notes
- Moisture content was measured with an infrared moisture analyzer at 105°C for 10 minutes.
- Mechanical properties were measured on injection molded parts made directly from the 50% NuPlastiQ / 50% polyethylene masterbatch.
- The reported film properties are for a monolayer blown film that was let-down with 50% additional LLDPE to a concentration of 25% NuPlastiQ. The thickness was 1.0 mil, and the blow-up ratio was 2.5:1.
- These values are typical properties only and should not be used for specification purposes. End users should confirm results with their own tests.
Value | Units | Test Method / Conditions | |
Ultimate Tensile Strength | 16.7 | MPa | D638 |
Tensile Strength at Break | 8.4 | MPa | D638 |
Izod - Notched | 61 | J/m | ASTM D256 |
Tensile Elongation at Break | 62 | % | D638 |
Tensile Secant Modulus (at 1%) | 430 | MPa | D638 |
Value | Units | Test Method / Conditions | |
Density | 1.16 | g/cm3 | ASTM D792 |
Value | Units | Test Method / Conditions | |
Moisture Content | max. 0.5 | % | ASTM D6980 |
Value | Units | Test Method / Conditions | |
Melting Temperature Range | 114 | °C | ASTM D3418 |
Melt Flow Index | 0.65 | g/10 min (190 °C/5 kg) | ASTM D1238 |
Value | Units | Test Method / Conditions | |
Tensile Strength MD (3) | 4940 | psi | ASTM D882 |
Tensile Strength TD (3) | 4190 | psi | ASTM D882 |
Elongation at Break MD (3) | 570 | % | ASTM D882 |
Elongation at Break TD (3) | 670 | % | ASTM D882 |
Elmendorf Tear MD (3) | 390 | g | ASTM D1922 |
Elmendorf Tear TD (3) | 590 | g | ASTM D1922 |
Dart Drop Test (3) | 290 | g | ASTM D1709 |
Value | Units | Test Method / Conditions | |
Flexural Modulus | 690 | MPa | D790 |
Regulatory & Compliance
- Certifications & Compliance
Technical Details & Test Data
- Viscosity Curve
Viscosity Curves at 190°C
- The MFI of XP 24250 is lower than the MFI of a typical blown film grade of LLDPE ( < 10 1/s). However, as shown above XP 24250 exhibits shear thinning behavior and performs closer to a standard film grade LLDPE under typical blown film conditions (200 1/s).
Packaging & Availability
- Packaging Type
Storage & Handling
- Storage and Drying
- BioLogiQ BioBlends are dried after production and shipped in sealed moisture-proof bags that are ready to use as supplied. They should be stored indoors in the sealed container away from heat until used.
- If pellets are exposed to a humid environment, they will absorb moisture from the air. If needed, dry pellets by introducing warm dry air at no more than 80°C for 1-4 hours.
- The estimated moisture content of a BioLogiQ BioBlend can be measured with an infrared moisture analyzer at 105°C for 10 minutes. The result of the measurement will not perfectly equal the moisture content, due to possible partial evaporation of plasticizer. The result from this test should be <0.5% moisture prior to processing.