Identification & Functionality
- Chemical Family
- Reinforcement Form
- Reinforcement Material
- Composite Materials Functions
- Technologies
- Product Families
Features & Benefits
- Features
- Milled fibers are aligned in the Z‐axis (i.e. orthogonal to fabric)
- Areal weight and ply thickness of the base fabric is increased
- Better damage tolerance & Z‐axis conductivity
- Retain key in‐plane properties with less in‐plane fiber
Applications & Uses
- Applications
- Composites End Use
- Composites Processing Methods
Properties
Technical Details & Test Data
- Compatibility
Supercomp dry products can be used in RTM/VARTM and wet layup or they can be supplied as prepregs for compression molding, autoclave, or out‐ofautoclave processing. Thermoplastic composites have also been made using Supercomp products. Contact Boston Materials for any questions about the compatibility of Supercomp products for your application.
- Comparative Properties
A test panel made with two layers of Supercomp 1015 Bi‐Axial prepreg was tested against a baseline test panel made with four layers of 3Kx3K plain weave prepreg. The two Supercomp 1015 Bi‐Axial layers were oriented such that their Z‐axis milled fiber surfaces faced each other at the mid‐plane. Both panels used a 250°F cure epoxy (Newport NB 301) and were cured at 50 psi for 1 hour via compression molding. Test coupons were machined from the panels using an abrasive water jet.
Test Standard Supercomp 1015 Axial Baseline Unit Z‐axis Thermal Conductivity ASTM E1461 1.52 0.68 W/m‐K Flexural Strength ASTM D790 546 511 MPa Flexural Modulus ASTM D790 25.4 20.1 GPa In‐Plane Tensile Strength ASTM D3039 547 751 MPa In‐Plane Compression Strength ASTM D6641 467 423 MPa - Physical Properties
Supercomp 1015 Bi-Axial Baseline Unit In‐Plane Fiber T300, 3K x 3K, Plain Weave T300, 3K x 3K, Plain Weave - Z‐Axis Fiber PX30, 150µm, Milled - - Ply Thickness @ 55% FV 0.38 [0.015] 0.20 [0.008] mm [in] Total Fiber Areal Weight 370 200 g/m2 In‐Plane Fiber Areal Weight 200 200 g/m2 Z‐axis Fiber Areal Weight 170 0 g/m2