Cardinal Paint - FS 13538 YELLOW 90 GLOSS T009-YL14

Identification & Functionality

Features & Benefits

Ready-to-Use Product Features: Acid Resistant,
Alkali Resistant,
Chemical Resistant,
Corrosion Resistant,
Excellent Solvent Resistance,
Good Smoothness,
High Gloss,
Oil Resistant

Applications & Uses

Markets: Paints & Coatings
Applications: Paints & Coatings — Other Paints & Coatings Applications
Application Method: Spray
Compatible Substrates & Surfaces: Aluminum,
Galvanized Steel,
Metal,
Steel
Application: This product was designed to be applied by electrostatic spray, on steel , galvanized steel, or aluminum. Most powders can be reclaimed, sieved and recycled, if proper housekeeping is maintained.
Pre Treatment: The substrate pretreatment prior to powder coating is a critical factor in developing maximum corrosion resistance and maximizing the life time of the product.

C.R.S. (Iron phosphate) 2 to 5 stages depending upon soil level, and quality desired.

C.R.S. (Zinc phosphate) 5 to 9 stages depending upon soil level, and quality desired.

Galvanized steel (Zinc phosphate)
5 to 7 stages depending on soil level, and quality desired. Galvanized steel must be degassed at 5 degrees above cure temperature to minimize gassing.

Aluminum (Chromate) 5 stage system is normally needed.

Aluminum (phosphate) 5 stage system is normally needed.

Properties

Color: Yellow
Cured Properties
Powder Characteristics
Cured Film Properties: All tests were performed a film thickness of 2.5 - 4.0 mils.

	Value	Units	Test Method / Conditions
All tests were performed at a film thickness of	2.5 - 4.0	mils	—
Cross Hatch Adhesion	4B	—	D3359B
Direct Impact	120.0	in.lbs.	D2794
Flexibility(Conical Mandrel)	100.0	%	D1737/D522
Gloss (at 60°)	90.0	%	D523
Indirect Impact	120.0	in.lbs.	D2794
Pencil Hardness	2H	—	D3363

Regulatory & Compliance

Technical Details & Test Data

Chemical and Corrosion Exposure Tests: Chemical Resistance: Good to excellent resistance to most solvents, oils, acids, and al kalies.

Overbake Resistance: Slight yellowing is evident, especially in white and pastel colors.

All tests were performed on 24 gage Bonderite 1000 panels.

Storage & Handling

Cardinal Paint and Powder FS 13538 YELLOW 90 GLOSS T009-YL14

C.R.S. (Iron phosphate)	2 to 5 stages depending upon soil level, and quality desired.
C.R.S. (Zinc phosphate)	5 to 9 stages depending upon soil level, and quality desired.
Galvanized steel (Zinc phosphate)	5 to 7 stages depending on soil level, and quality desired. Galvanized steel must be degassed at 5 degrees above cure temperature to minimize gassing.
Aluminum (Chromate)	5 stage system is normally needed.
Aluminum (phosphate)	5 stage system is normally needed.