Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Product Type
- Technologies
- Product Families
Features & Benefits
- Ready-to-Use Product Features
Applications & Uses
- Markets
- Compatible Substrates & Surfaces
- Suggested Applications
- Epoxy Glass Lamination: Excellent wetting out properties
- Thin Glue-Line Bonding: No bulky filler to occupy space
- Void-Free, See Through Castings: Low viscosity, air released rapidly
- Room Temperature Cure
- H-1 Hardener: Offers a working time of 30 minutes. Cures in 6 hours at 25°C or 30 minutes at 65°C. Produces a tough, rigid resin with good dimensional stability. Do not heat cure if the mass exceeds 100 grams.
- H-18 Hardener: Offers a working time of 45 minutes. Cures in 24 hours at 25°C or 2 hours at 65°C. Produces a tough, resilient resin with good mechanical and thermal shock properties.
- H-10LV Hardener: Offers a working time of 3 hours. Cures in 24 hours at 225°C or 3 hours at 65°C. Produces a variable hardness resin with excellent impact properties.
- Mixing Instructions
Weigh out the desired amount of resin in a clean container. Add the hardener accurately by weight in the proper proportion as specified above. (ie. 14 grams of H-1 Hardener and 100 grams of CC3-105 for a total mix of 114 grams) Mix thoroughly. Use in a well ventilated area and avoid contact with eyes and skin.
Properties
- Color
- Physical & Electrical Properties
| Value | Units | Test Method / Conditions | |
| Bond Shear Strength (1 in Overlap) | 2000.0 | psi | — |
| Dielectric Strength | 380.0 | volts/mil | — |
| Flexural Strength | 9000.0 | psi | — |
| Izod Impact (of Notch) | 0.5 | ft lbs/in | — |
| Service Temperature (Continuous) | -55 - 150 | °C | — |
| Specific Gravity (Uncatalyzed, 25°C) | 1.05 | — | — |
| Thermal Conductivity | 0.2 | W/mK | — |
| Viscosity (Uncatalyzed, 25°C) | 500 - 700 | cps | — |
| Volume Resistivity (25°C) | 1013.0 | ohm-cm | — |
| Water Absorption (7 days, 25°C) | 0.13 | % | — |
Technical Details & Test Data
- Choice of Hardeners
- H-1 Hardener: Rigid, good dimensional stability, fast cure.
- H-18 Hardener: Resilient, excellent mechanical and thermal shock, low viscosity, good air release, fast cure.
- H-10LV Hardener: Variable hardness, excellent impact properties, long pot life
HARDENER PARTS BY WEIGHT PER 100 PARTS OF RESIN POT LIFE 100 GRAM 25°C (77°F) CURE TIME 25°C (77°F) CURE TIME 65°C (149°F) CURE TIME 125°C (257°F)
H-1 Hardener 14 30 min. 6 hrs. 30 mins. 15 min. H-18 Hardener 29 45 min. 24 hrs. 2 hrs. 20 min. H-10LV Hardener 33 (rigid) 3 hrs. 24 hrs. 3 hrs. - - - H-10LV Hardener 83 (semi-flex) 3 hrs. 24 hrs. 3 hrs. - - - H-10LV Hardener 133 (flexible) 3 hrs. 24 hrs. 3 hrs. - - -