CIM 1061 is a liquid applied urethane coating that:
- ANSI/NSF 61 approved for potable water contact up to 82°C.
- Excellent wear and abrasion resistance.
- Cures in hours to form a tough elastomeric coating
- Ideal for coating concrete
- Advantages
CIM 1061 is one of the toughest coatings available, specifically formulated to meet the demanding needs of the water/wastewater industries
- Ideal for coating concrete.
- ANSI/NSF 61 certified for potable water contact up to 180°F.
- Tested to ANSI 118.10-199, "Standard Specification for Load Bearing, Bonded, Waterproof Membrane for Thin-Set Ceramic Tile and Dimension Stone Installation".
- Forms a tough elastomeric coating able to bridge cracks and joints.
- Meets the most demanding health and safety requirements for drinking water, fish hatcheries, and food processing plants.
- Adheres to and bridges between common construction materials such as concrete, steel, glass, wood, and most coatings.
- Environmentally sound, complying with the toughest VOC standards.
- Can be repaired when damaged or when new tank penetrations are installed.
- Excellent wear and abrasion service.
- UV stable.
- Bonds to most substrates
- Excellent adhesion provides a fully bonded waterproofing system
- Approved to ANSI/NSF 61 Standard
- Suitable for contact with potable water for tanks as small as 5,000 gallons
- Lowest permeability in industry
- Designed for constant immersion environments
- High solids/low VOC
- Compliant to toughest VOC regulations
- Suitable for applications in direct contact with UV
- Excellent chemical resistant
- Resistant to strong acids and bases
- Excellent Concrete Crack Bridging
- Bridge new cracks up to ¼ inch
- Liquid, two-component urethane can be applied to complex tanks with multiple penetrations, and irregular shapes.
Applications & Uses
- Markets
- Application Area
- Surface Preparation
General
- Substrates must be clean and surface dry with no oils, grease or loose debris.
- Perform adhesion tests to confirm adequacy of surface preparation.
Concrete
- ICRI-CSP 4-6 surface profile exposing aggregate.
- Concrete must exhibit minimum 3,000 psi compressive strength and be free of release agents and curing compounds.
- The substrate must be clean, surface dry and free of contaminates.
Steel
- Minimum 3 mil profile.
- Immersion service – SSPC-SP10 / NACE No. 2 Near White Blast.
- Non-Immersion service – SSPC-SP6 / NACE No. 3 Commercial Blast.
Other Metals
SSPC-SP1 solvent clean and abrasive blast to roughen and degloss the surface. Use CIM Bonding Agent for greater adhesion.
Glass
Thoroughly clean. ClIM Bonding Agent must be used for increased adhesion. For immersion service roughen the surface.
Previous Coatings and Linings
CIM 1061 may be applied over some existing coatings and linings and achieve acceptable performance. CIM Bonding Agent is recommended for greater adhesIon. inished system results vary due to a variety of project specitic tactors, including the service conditions to which the system is exposed. Iherefore, .I.M. Industries does not accept responsibility for determining the suitability of an existing coating or lining as a substrate for CIM products. Owner shall perform adhesion tests on any existing coating or lining to etermine suitability.
Earth : Use CIM Scrim
Color
CIM 1061 is initially shiny black, turning dull over 3 to 6 months when exposed to direct sunlight. For a colored or reflecting surface finish.
- Temperature Conditions
Surface should be at least 50°F (10°C) and must be 5°F (3°C) above the dew point. Do not apply when the substrate or ambient temperature is rising or coating is in direct sunlight. CIM 1061 should be at least 60°F (15°C) when mixed and applied. ClM 1061 may be preheated to faciltate application at low temperatures, but working time will be reduced.
- Mixing
DO NOT THIN. DO NOT HAND MIX. Begin mixing each pail (4.4 gal.) of CIM 1061 Premix using a pOwer mixer (e.g. 2 drill and an eight inch mud mixer). Do not draw air into the mix. While mixing, slowly add one jug (0.6 gal.) of CIM 1061 Activator to the pail and mix thoroughly for 3 full minutes. The proportions are premeasured; DO NOT ESTIMATE. Mixing Jigs and Timers from C.I.M. Industries help eliminate mixing errors and increase productivity on the job.
- Application
Apply CIM 1061 directly to a clean and dry substrate. Vertical surfaces will require multiple coats.
Equipment
Spray equipment requires large diameter hose and air supplied mastic gun or plural component spray equipment. Roller, squeegee, and trowel may also be used.
Priming
Porous substrates such as wood and concrete may be primed with CIM Epoxy Primer to minimize outgassing. The maximum recoat window for CIM Epoxy Primer is 48 hours. See the CIM Epoxy Primer lechnical Data sheet for additional intormation. Pertorm adhesion tests to confirm adequacy of adhesIon to primer.
Recoating
CIM 1061 may be recoated in 1 hour and must be recoated soon after the coating no longer comes off on polyethylene (typically within 4 hours of mixing). If the coating has cured longer than this time, the surface must be severely abraded using surface grinder or other mechanical means, and be free of dust and debris. Use CIM Bonding Agent for better adhesion. For immersion conditions, all coats shall be applied within four hours of each other, except at joint lines.
Recommended Minimum Thickness
Recommended minimum thickness of the coating is 60 wet mils. Additional thickness may be specified, but extended time is required to insure proper solvent release prior to placing the liner in service.
Curing Time
Before placing the coating into potable water service or similar applications, allow sufficient time for solvents to release from the coating. The required time for a 60 wet mil co0ating is
two weeks at 60°F (15°C) and varies depending upon coating thickness and substrate temperature. For many other applications, CIM 1061 may be placed into service in 24 hours.
.
DisinfectionCIM 1061 coating must be washed, rinsed, and disinfected in accordance with C.I.M. Industries Instruction Guide "Decontamination or Washing Procedures for Potable Water
Tank and Fish Pond Service" (IG-10).
Clean-upUse mineral spirits for clean-up of uncured material. Spray equipment must be flushed regularly during application to prevent material from setting up in the hose and pump. Cured
material is very difficult to remove. Soaking in solvent will soften the material and may assist in its removal.
Properties
- Typical Properties
| Value | Units | Test Method / Conditions | |
| Solids by Volume (1416 dry mils x sq. ft./gal.) | 88.0 | % | — |
| VOC | 90 (0.75) | g/l (lb./gal.) | — |
| Abrasion Resistance (Loss) | 1.2 | mg | ASTM D4060 CS-17 Wheel, 1000 rev |
| Adhesion to Concrete (Dry) | 350.0 | psi | Elcometer |
| Deflection Temperature (Minimum Use Temperature) | max. -60 | ºF | ASTM D648 |
| Density Premix | 8.0 | Ibs./gal. | — |
| Density Activator | 10.1 | Ibs./gal. | — |
| Density Mixed & Cured | 8.3 | Ibs./gal. | — |
| Elastomeric Waterproofing | Exceeds all criteria | — | ASTM C836 |
| Elastomeric Waterproofing | Exceeds all criteria | — | ASTM C957 |
| Extension to Break | 300.0 | % | ASTM D412 |
| Flooring and Shower Lining | Pass | — | UPC/IBC ANSI 118.10 |
| Green Roof Membrane/Root Barrier | Pass | — | ANSI/GRHC/SPRI VR-1 2011 |
| Hardness | 65.0 | Shore A | ASTM D2240 at 77ºF |
| Liner Performance (Crack Bridging 10 cycles at -15ºF) | min. 1/8 | ” | — |
| Liner Performance (Crack Bridging After Heat Aging) | min. 1/4 | ” | — |
| Liner Weight (60 mil wet film thickness) | 31.0 | lbs./100 sq. ft. | — |
| Mix Ratio Weight | 6.2:1 | — | — |
| Mix Ratio Volume | 7.8:1 | — | — |
| Permeability to Water Vapor | 0.03 | perms | ASTM E96 Procedure B,100 mil sheet |
| Potable Water Service ANSI/NSF | 61 - 180 | °F | UL File Number MH17445 WQA Certified |
| Recovery from 100% extension (After 5 minutes) | 98.0 | % | — |
| Recovery from 100% extension (After 24 hours) | 100.0 | % | — |
| Service Temperature | -60 to 220 | ºF | — |
| Softening Point, Ring & Ball | min. 325 | ºF | ASTM D36 |
| Tear Strength | 180.0 | lbs./in. | ASTM D624 (Die C) |
| Tensile Strength | 1000.0 | psi | ASTM D412,100 mil sheet |
| Weathering | 5000 | hours | ASTM D822 |
| Flash Point Premix | 101.0 | ºF | — |
| Flash Point Activator | min. 400 | ºF | — |
Regulatory & Compliance
- Certifications & Compliance
Safety & Health
- Precautions
Avoid contamination with water or moisture. Keep all pails and jugs tightly closed until ready for use. All equipment, air supplies, and application substrates must be ABSOLUTELY DRY. Do not apply in wet weather or when rain is imminent or when the CIM 1061 or the substrate may become wet within 4 hours after coating. Use caution when applying CIM 1061 in confined spaces.
- Safety Information
This product contains petroleum asphalt, petroleum distillates, amine compounds and/or other chemical ingredients. Adequate health and safety precautions should be observed during the storage, handling, application and curing.
Warning Flammable. Use only in well ventilated areas. Do not store or use near open flame, sparks or hot sufaces. Keep tightly closed. Avoid contact with moisture or water. Keep out of reach of children.
Packaging & Availability
- Packaging
CIM 1061 is available in mixed units of O.8 gallons and 5 gallons. Each unit consists of a container of premix and a smaller container of activator. Quantities have been premeasured
to provide the proper mixing ratio, leaving sufficient room in the premix container to facilitate adequate mixing. Do not estimate proportions.
Storage & Handling
- Shelf Life
- 1 year (Activator), 2 years (Premix)
- Storage
- Store at 20°F to 110°F temperature for NFPA Class II.
- Store at 70°F to 95°F temperature for NFPA Class III B.
*Reclassed based on container size and physical properties.
- Pot Life
About 30 minutes. Working time depends on temperature and method of application. Working time for spray applications will be significantly shorter.