Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
- Features
- Flame retardant
- Heat resistance
- Balanced mechanical properties
Applications & Uses
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
- Uses
- Electrical electronic applications
- Automotive applications
- Connectors
- Processing Method
Injection Molding
Properties
- Flame Rating
- Mechanical Properties
- Typical Properties
- Thermal Properties
- Flammability
Value | Units | Test Method / Conditions | |
Tensile Modulus | 8300 | MPa | ASTM D638 |
Tensile Strength | 85 | MPa | ASTM D638 |
Tensile Elongation Break | 2 | % | ASTM D638 |
Flexural Modulus | 7100 | MPa | ASTM D790 |
Flexural Strength | 129 | MPa | ASTM D790 |
Value | Units | Test Method / Conditions | |
Specific Gravity | 1.59 | g/cm3 | ASTM D792 |
Molding Shrinkage (3.2 mm) | 0.50 - 1.00 | % | ASTM D955 |
Water Absorption - 24hr | 1.4 | % | ASTM D570 |
Notched Izod Impact (23°C) | 87 | J/m | ASTM D256 |
Drying Temperature | 80 - 100 | °C | — |
Drying Time | 2 - 4 | hr | — |
Rear Temperature | 220 - 230 | °C | — |
Middle Temperature | 230 - 240 | °C | — |
Front Temperature | 240 - 250 | °C | — |
Nozzle Temperature | 250 - 260 | °C | — |
Mold Temperature | 80 - 100 | °C | — |
Value | Units | Test Method / Conditions | |
Deflection Temperature Under Load (1.8 MPa, Unannealed, 4.0 mm) | 169 | °C | ASTM D648 |
Value | Units | Test Method / Conditions | |
Flame Rating (1.6 mm) | V-0 | — | UL94 |
Regulatory & Compliance
- Certifications & Compliance