Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
- Features
- Flame retardant
- Unfilled
Applications & Uses
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
- Uses
- Electrical/electronics components
- Automotive components
- Processing Method
Injection Molding
Properties
- Flame Rating
- Mechanical Properties
- Typical Properties
- Thermal Properties
- Flammability
Value | Units | Test Method / Conditions | |
Tensile Modulus | 1325 | MPa | ASTM D638 |
Tensile Strength | 26 | MPa | ASTM D638 |
Tensile Elongation Break | 38 | % | ASTM D638 |
Flexural Modulus | 1275 | MPa | ASTM D790 |
Flexural Strength | 41 | MPa | ASTM D790 |
Value | Units | Test Method / Conditions | |
Specific Gravity | 1.16 | g/cm3 | ASTM D792 |
Rockwell Hardness | 90 | Scale R | ASTM D785 |
Melt Flow Rate (220°C/10 kg) | 21 | g/ 10 min | ASTM D1238 |
Molding Shrinkage (3.2 mm) | 1.20 - 1.40 | % | ASTM D955 |
Water Absorption - 24hr | 0.01 | % | ASTM D570 |
Notched Izod Impact (23°C) | 28 | J/m | ASTM D256 |
Drying Temperature | 60 - 80 | °C | — |
Drying Time | 2 - 4 | hr | — |
Rear Temperature | 180 - 190 | °C | — |
Middle Temperature | 190 - 200 | °C | — |
Front Temperature | 190 - 200 | °C | — |
Nozzle Temperature | 200 - 210 | °C | — |
Mold Temperature | 30 - 60 | °C | — |
Value | Units | Test Method / Conditions | |
Deflection Temperature Under Load (0.45 MPa, Unannealed, 4.0 mm) | 109 | °C | ASTM D648 |
Value | Units | Test Method / Conditions | |
Flame Rating (1.6 mm) | V-0 | — | UL94 |
Regulatory & Compliance
- Certifications & Compliance