Knowde Enhanced TDS
Identification & Functionality
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
- Features
- High impact resistance
- Good processability
- Good dimensional stability
- High rigidity
- High heat resistance
- Good color stability
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
- Uses
- Portable appliances
- Automotive applications
- Electrical/electronic applications
- Business equipment
- Processing Method
Injection Molding
Properties
- Flame Rating
- Mechanical Properties
- Typical Properties
- Thermal Properties
- Flammability
Value | Units | Test Method / Conditions | |
Tensile Modulus | 2516 | MPa | ASTM D638 |
Tensile Strength | 58 | MPa | ASTM D638 |
Tensile Elongation Break | 50 | % | ASTM D638 |
Flexural Modulus | 2578 | MPa | ASTM D790 |
Flexural Strength | 97 | MPa | ASTM D790 |
Value | Units | Test Method / Conditions | |
Specific Gravity | 1.15 | g/cm3 | ASTM D792 |
Rockwell Hardness | 120 | Scale R | ASTM D785 |
Melt Flow Rate (260°C/5 kg) | 20 | g/ 10 min | ASTM D1238 |
Melt Flow Rate (260°C/2.16 kg) | 12 | g/ 10 min | ASTM D1238 |
Molding Shrinkage (3.2 mm) | 0.40 - 0.60 | % | ASTM D955 |
Water Absorption - 24hr | 0.1 | % | ASTM D570 |
Notched Izod Impact (23°C) | 755 | J/m | ASTM D256 |
Drying Temperature | 80 - 90 | °C | — |
Drying Time | 4 - 6 | hr | — |
Rear Temperature | 210 - 250 | °C | — |
Middle Temperature | 220 - 260 | °C | — |
Front Temperature | 225 - 270 | °C | — |
Nozzle Temperature | 230 - 270 | °C | — |
Mold Temperature | 50 - 90 | °C | — |
Value | Units | Test Method / Conditions | |
Deflection Temperature Under Load (0.45 MPa, Unannealed, 4.0 mm) | 132 | °C | ASTM D648 |
Deflection Temperature Under Load (1.8 MPa, Unannealed, 4.0 mm) | 110 | °C | ASTM D648 |
Value | Units | Test Method / Conditions | |
Flame Rating (1.6 mm) | HB | — | UL94 |
Regulatory & Compliance