Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
- Features
- Talc Filled, 20%
- Good Impact Strength
- Good Heat Resistance
- Good dimensional stability
Applications & Uses
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
- Uses
- Appliances Applications
- Electrical / Electronic Parts
- Processing Method
Injection Molding
Properties
- Flame Rating
- Mechanical Properties
- Typical Properties
- Thermal Properties
- Flammability
Value | Units | Test Method / Conditions | |
Tensile Strength | 34 | MPa | ASTM D638 |
Tensile Elongation Break | 70 | % | ASTM D638 |
Flexural Modulus | 2700 | MPa | ASTM D790 |
Flexural Strength | 57 | MPa | ASTM D790 |
Value | Units | Test Method / Conditions | |
Specific Gravity | 1.05 | g/cm3 | ASTM D792 |
Melt Flow Rate (230°C/2.16 kg) | 10 | g/ 10 min | ASTM D1238 |
Molding Shrinkage (3.2 mm) | 1.00 - 1.40 | % | ASTM D955 |
Notched Izod Impact (23°C) | 50 | J/m | ASTM D256 |
Drying Temperature | 100 | °C | - |
Drying Time | 2 - 4 | hr | - |
Rear Temperature | 180 - 190 | °C | - |
Middle Temperature | 190 - 200 | °C | - |
Front Temperature | 200 - 210 | °C | - |
Nozzle Temperature | 210 - 220 | °C | - |
Processing (Melt) Temp | 190 - 220 | °C | - |
Mold Temperature | 60 - 70 | °C | - |
Value | Units | Test Method / Conditions | |
Deflection Temperature Under Load (0.45 MPa, Unannealed, 4.0 mm) | 124 | °C | ASTM D648 |
Deflection Temperature Under Load (1.8 MPa, Unannealed, 4.0 mm) | 78 | °C | ASTM D648 |
Value | Units | Test Method / Conditions | |
Flame Rating (1.6 mm) | HB | - | UL94 |
Regulatory & Compliance
- Certifications & Compliance