Features & Benefits
- Features
- PTFE Filled, 5%
- Low Friction
- Good chemical resistance
- Good wear resistance
- Lubricated
- Good thermal stability
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
- Uses
- Mechanical parts
- Automotive applications
- Plastic gears
- Bushing & sliding components
- Processing Method
Injection Molding
Properties
- Flame Rating
- Mechanical Properties
- Thermal Properties
- Typical Properties
- Flammability
Value | Units | Test Method / Conditions | |
Tensile Strength | 44 | MPa | ASTM D638 |
Tensile Elongation Break | 25 | % | ASTM D638 |
Flexural Modulus | 2500 | MPa | ASTM D790 |
Flexural Strength | 73 | MPa | ASTM D790 |
Value | Units | Test Method / Conditions | |
Deflection Temperature Under Load (1.8 MPa, Unannealed, 4.0 mm) | 100 | °C | ASTM D648 |
Value | Units | Test Method / Conditions | |
Specific Gravity | 1.09 | g/cm3 | ASTM D792 |
Molding Shrinkage (3.2 mm) | 0.50 - 0.60 | % | ASTM D955 |
Notched Izod Impact (23°C) | 150 | J/m | ASTM D256 |
Coefficient of Friction (vs Steel - dynamic) | 0.4 | - | ASTM D1894 |
Coefficient of Friction (vs Steel - Static) | 0.27 | - | ASTM D1894 |
Drying Temperature | 80 | °C | - |
Drying Time | 2 - 4 | hr | - |
Rear Temperature | 220 - 225 | °C | - |
Middle Temperature | 225 - 230 | °C | - |
Front Temperature | 230 - 235 | °C | - |
Nozzle Temperature | 235 - 240 | °C | - |
Processing (Melt) Temp | 220 - 240 | °C | - |
Mold Temperature | 60 - 70 | °C | - |
Value | Units | Test Method / Conditions | |
Flame Rating (1.6 mm) | HB | - | UL94 |