Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Features
- PTFE Filled, 10%
- Low Friction
- Good chemical resistance
- Good wear resistance
- Lubricated
- Good thermal stability
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
- Uses
- Mechanical parts
- Automotive applications
- Plastic gears
- Bushing & sliding components
- Processing Method
Injection Molding
Properties
- Flame Rating
- Mechanical Properties
- Typical Properties
- Thermal Properties
- Flammability
Value | Units | Test Method / Conditions | |
Tensile Strength | 52 | MPa | ASTM D638 |
Tensile Elongation Break | 10 | % | ASTM D638 |
Flexural Modulus | 2630 | MPa | ASTM D790 |
Flexural Strength | 80 | MPa | ASTM D790 |
Value | Units | Test Method / Conditions | |
Specific Gravity | 1.24 | g/cm3 | ASTM D792 |
Molding Shrinkage (3.2 mm) | 0.50 - 0.80 | % | ASTM D955 |
Notched Izod Impact (23°C) | 190 | J/m | ASTM D256 |
Coefficient of Friction (vs Steel - dynamic) | 0.25 | - | ASTM D1894 |
Coefficient of Friction (vs Steel - Static) | 0.08 | - | ASTM D1894 |
Drying Temperature | 120 | °C | - |
Drying Time | 4 - 6 | hr | - |
Rear Temperature | 275 - 280 | °C | - |
Middle Temperature | 280 - 285 | °C | - |
Front Temperature | 285 - 290 | °C | - |
Nozzle Temperature | 290 - 295 | °C | - |
Processing (Melt) Temp | 275 - 300 | °C | - |
Mold Temperature | 85 - 110 | °C | - |
Value | Units | Test Method / Conditions | |
Deflection Temperature Under Load (1.8 MPa, Unannealed, 4.0 mm) | 130 | °C | ASTM D648 |
Value | Units | Test Method / Conditions | |
Flame Rating (1.6 mm) | HB | - | UL94 |
Regulatory & Compliance
- Certifications & Compliance