Features & Benefits
- Features
- PTFE Filled, 10%
- Low Friction
- Good chemical resistance
- Good wear resistance Lubricated
- Good thermal stability
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
- Uses
- Mechanical parts
- Automotive applications
- Plastic gears
- Bushing & sliding components
- Processing Method
Injection Molding
Properties
- Flame Rating
- Mechanical Properties
- Typical Properties
- Thermal Properties
- Flammability
Value | Units | Test Method / Conditions | |
Tensile Strength | 56 | MPa | ASTM D638 |
Tensile Elongation Break | 15 | % | ASTM D638 |
Flexural Modulus | 2200 | MPa | ASTM D790 |
Flexural Strength | 80 | MPa | ASTM D790 |
Value | Units | Test Method / Conditions | |
Specific Gravity | 1.45 | g/cm3 | ASTM D792 |
Molding Shrinkage (3.2 mm) | 2.00 - 3.00 | % | ASTM D955 |
Notched Izod Impact (23°C) | 56 | J/m | ASTM D256 |
Coefficient of Friction (vs Steel - dynamic) | 0.32 | — | ASTM D1894 |
Coefficient of Friction (vs Steel - Static) | 0.28 | — | ASTM D1894 |
Drying Temperature | 80 | °C | — |
Drying Time | 4 - 6 | hr | — |
Rear Temperature | 180 - 185 | °C | — |
Middle Temperature | 185 - 190 | °C | — |
Front Temperature | 190 - 200 | °C | — |
Nozzle Temperature | 200 - 210 | °C | — |
Processing (Melt) Temp | 180 - 215 | °C | — |
Mold Temperature | 80 - 105 | °C | — |
Value | Units | Test Method / Conditions | |
Deflection Temperature Under Load (0.45 MPa, Unannealed, 4.0 mm) | 108 | °C | ASTM D648 |
Value | Units | Test Method / Conditions | |
Flame Rating (1.6 mm) | HB | — | UL94 |