Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Product Type
- Technologies
- Suitable Lamp Types
LED 365 nm, LED 400 nm, UVA
Features & Benefits
- Ready-to-Use Product Features
- Special Features
- compliant with RoHS Directive 2015/863/EU
- compliant with limits of VOC content in adhesive acc. to GB33372-2020
- Function
Electronic adhesive
Applications & Uses
- Applications
- Cure Method
- Typical Area Of Use
- -40 - 120 °C
- pin potting
- pin sealing
- General Curing and Processing Information
The curing time stated in the technical data was determined in the laboratory. It can vary depending on the adhesive quantity and component geometry and is therefore a reference value.The heating time of the components must be added to the actual curing time. It depends on component size and type of heat input. The specified curing temperature must be reached directly at the adhesive.Increasing or decreasing the curing temperature and / or irradiation intensity and / or irradiation time shortens or prolongs the curing time and can lead to changed physical properties.All curing or light fixation parameters depend on material thickness and absorption, adhesive layer thickness, lamp type and distance between lamp and adhesive layer.Values measured after 24 h at approx. 23 °C / 50 % r.h., unless otherwise specified.
Properties
- Typical Properties
- Processing Parameters
Value | Units | Test Method / Conditions | |
Typical Light Fixation Time (Intensity 55 - 60 Mw/Cm² Uva) | 4.0 | s | — |
Typical Light Fixation Time (Intensity 200 Mw/Cm² Led 400 Nm) | 2.0 | s | — |
Typical Curing Time (At+110 °C In Air Convection Oven) | 5.0 | min | — |
Typical Curing Time (At +130 °C In Air Convection Oven) | 3.0 | min | — |
Conditioning Time (Typical) (When Stored In Cold Conditions In Containers Up To 50 Ml) | 30.0 | min | — |
Conditioning Time (Typical) (When Stored In Cold Conditions In Containers Up To 1, 000 Ml) | 4.0 | h | — |
Processing Time (At Rt Approx. +23 °C In Containers Up To 50 M) | 14.0 | d | — |
Processing Time (At Rt Approx. +23 °C In Containers Up To 170 M) | 5.0 | d | — |
Processing Time (At Rt Approx. +23 °C In Containers Up To 900 M) | 24.0 | h | — |
Color In Uncured Condition | Red | — | — |
Color In Cured Condition In 0.1 Mm Layer Thickness | Red | — | — |
Fluorescence | Fluorescent | — | — |
Value | Units | Test Method / Conditions | |
Density (Delo Standard 13 | Liquid) | 1.05 | g/cm³ | — |
Viscosity Liquid | Rheometer | Shear Rate: 2 1/S | Gap: 500 Μm | 14500.0 | mPa·s | — |
Viscosity Liquid | Rheometer | Shear Rate: 10 1/S | Gap: 500 Μm | 6500.0 | mPa·s | — |
Compression Shear Strength Delo Standard 5 | Glass | Al | 60 Mw/Cm² | 60 S | 22.0 | MPa | — |
Compression Shear Strength Delo Standard 5 | Glass | Stainless Steel | 60 Mw/Cm² | 60 S | 19.0 | MPa | — |
Compression Shear Strength Delo Standard 5 | Glass | Fr4 | 60 Mw/Cm² | 60 S | 21.0 | MPa | — |
Compression Shear Strength Delo Standard 5 | Glass | Glass | 60 Mw/Cm² | 60 S | 22.0 | MPa | — |
Compression Shear Strength Delo Standard 5 | Glass | Pa66 | 60 Mw/Cm² | 60 S | 14.0 | MPa | — |
Compression Shear Strength Delo Standard 5 | Glass | Pbt | 60 Mw/Cm² | 60 S | 5.0 | MPa | — |
Tensile Strength 60 Mw/Cm² | 90 S | 17.0 | MPa | DIN EN ISO 527 |
Elongation At Tear | 60 Mw/Cm² | 90 S | 220.0 | % | DIN EN ISO 527 |
Young'S Modulus Based On 60 Mw/Cm² | 90 S | 320.0 | MPa | DIN EN ISO 527 |
Shore Hardness D (60 Mw/Cm² | 90 S) | 50.0 | — | DIN EN ISO 868 |
Glass Transition Temperature Delo Standard 24 | Liquid | Rheometer | 100.0 | °C | — |
Shrinkage Delo Standard 13 | 60 Mw/Cm² | 90 S | 5.6 | vol. % | — |
Regulatory & Compliance
- Certifications & Compliance
Technical Details & Test Data
- Converting Table
°F = (°C *1.8) +32
1 inch = 25.4 mm
1 mil = 25.4
1 oz = 28.3495 g
1 MPa = 145.04 psi
1 GPa = 145.04 ksi
1cP = 1 mPa•s
IN = 0.225 lb
Storage & Handling
- Storage Life
In Unopened Original Container (at 0°C To +10°C) is 6 months