Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Technologies
- Suitable Lamp Types
LED 365 nm, LED 400 nm, UVA
Features & Benefits
- Ready-to-Use Product Features
- Special Features
- compliant with RoHS Directive 2015/863/EU
- compliant with limits of VOC content in adhesive acc. to GB33372-2020
- passes ANSI/UL 94 HB Flame Test
Applications & Uses
- Markets
- Cure Method
- Typical Area Of Use
- -40 - 120 °C
- glass/metal bondings
- mixed bondings with plastics
- General Curing and Processing Information
The curing time stated in the technical data was determined in the laboratory. It can vary depending on the adhesive quantity and component geometry and is therefore a reference value.Increasing or decreasing the curing temperature and / or irradiation intensity and / or irradiation time shortens or prolongs the curing time and can lead to changed physical properties.All curing or light fixation parameters depend on material thickness and absorption, adhesive layer thickness, lamp type and distance between lamp and adhesive layer.Values measured after 24 h at approx. 23 °C / 50 % r.h., unless otherwise specified.
Properties
- Typical Properties
- Processing Parameters
| Value | Units | Test Method / Conditions | |
| Typical Light Fixation Time (Intensity 55 - 60 Mw/Cm² Uva) | 10.0 | s | — |
| Typical Light Fixation Time (Intensity 200 Mw/Cm² Led 400 Nm) | 4.0 | s | — |
| Conditioning Time (Typical) (When Stored In Cold Conditions In Containers Up To 50 Ml) | 30.0 | min | — |
| Conditioning Time (Typical) (When Stored In Cold Conditions In Containers Up To 1, 000 Ml) | 4.0 | h | — |
| Processing Time (At Rt Approx. +23 °C) | 28.0 | d | — |
| Color In Uncured Condition | Colorless | — | — |
| Color In Cured Condition In 0.1 Mm Layer Thickness | Colorless | — | — |
| Color In Cured Condition In 1 Mm Layer Thickness | Colorless | — | — |
| Value | Units | Test Method / Conditions | |
| Density (Liquid) | 1.04 | g/cm³ | DIN EN ISO 2811-3 |
| Viscosity Liquid | Rheometer | Shear Rate: 2 1/S | Gap: 500 Μm | 26000.0 | mPa·s | — |
| Viscosity Liquid | Rheometer | Shear Rate: 10 1/S | Gap: 500 Μm | 12000.0 | mPa·s | — |
| Thixotropy Index (Liquid | Rheometer | Gap: 500 Μm) | 4.0 | — | — |
| Compression Shear Strength (Delo Standard 5 | Glass | Al | 400 Nm | 200 Mw/Cm² | 10 S | Plus | At Approx. +23 °C | Rel. Air Humidity: 50 % | 72 H) | 6.0 | MPa | — |
| Compression Shear Strength Delo Standard 5 | Glass | Glass | 400 Nm | 200 Mw/Cm² | 10 S | Plus | At Approx. +23 °C | Rel. Air Humidity: 50 % | 72 H | 9.0 | MPa | — |
| Compression Shear Strength Delo Standard 5 | Glass | Pa6 | 400 Nm | 200 Mw/Cm² | 10 S | Plus | At Approx. +23 °C | Rel. Air Humidity: 50 % | 72 H | 11.0 | MPa | — |
| Compression Shear Strength Delo Standard 5 | Pc | Pc | 400 Nm | 200 Mw/Cm² | 10 S | Plus | At Approx. +23 °C | Rel. Air Humidity: 50 % | 72 H | 14.0 | MPa | — |
| Compression Shear Strength Delo Standard 5 | Pmma | Pmma | 400 Nm | 200 Mw/Cm² | 10 S | Plus | At Approx. +23 °C | Rel. Air Humidity: 50 % | 72 H | 8.0 | MPa | — |
| Tensile Strength 400 Nm | 200 Mw/Cm² | 60 S | Plus | At Approx. +23 °C | Rel. Air Humidity: 50 % | 72 H | 8.0 | MPa | DIN EN ISO 527 |
| Elongation At Tear | 400 Nm | 200 Mw/Cm² | 60 S | Plus | At Approx. +23 °C | Rel. Air Humidity: 50 % | 72 H | 270.0 | % | DIN EN ISO 527 |
| Young'S Modulus By The Criteria Of 400 Nm | 200 Mw/Cm² | 60 S | Plus | At Approx. +23 °C | Rel. Air Humidity: 50 % | 72 H | 45.0 | MPa | DIN EN ISO 527 |
| Shore Hardness A (By The Criteria Of | 400 Nm | 200 Mw/Cm² | 60 S | Plus | At Approx. +23 °C | Rel. Air Humidity: 50 % | 72 H) | 75.0 | — | DIN EN ISO 868 |
| Glass Transition Temperature Dmta | 400 Nm | 200 Mw/Cm² | 60 S | Plus | At Approx. +23 °C | Rel. Air Humidity: 50 % | 72 H | 96.0 | °C | — |
| Coefficient Of Linear Expansion (Delo Standard 26 | Tma | Evaluation T: 30 °C - 140 °C | 400 Nm | 200 Mw/Cm² | 60 S | Plus | At Approx. +23 °C | Rel. Air Humidity: 50 % | 72 H) | 217.0 | ppm/K | — |
| Shrinkage Delo Standard 13 | 400 Nm | 200 Mw/Cm² | 60 S | Plus | At Approx. +23 °C | Rel. Air Humidity: 50 % | 72 H | 4.6 | vol. % | — |
| Water Absorption By The Criteria Of 400 Nm | 200 Mw/Cm² | 60 S | Plus | At Approx. +23 °C | Rel. Air Humidity: 50 % | 72 H | Type Of Storage: Media | Medium: Distilled Water | Storage Temperature: At Approx. +23 °C | 2.5 | wt. % | DIN EN ISO 62 |
| (Dielectric Strength | 400 Nm | 200 Mw/Cm² | 60 S | Plus | At Approx. +23 °C | Rel. Air Humidity: 50 % | 72 H) | 20.0 | kV/mm | DIN EN 60243-1 |
Regulatory & Compliance
- Certifications & Compliance
Technical Details & Test Data
- Converting Table
°F = (°C *1.8) +32
1 inch = 25.4 mm
1 mil = 25.4
1 oz = 28.3495 g
1 MPa = 145.04 psi
1 GPa = 145.04 ksi
1cP = 1 mPa•s
IN = 0.225 lb
Storage & Handling
- Storage Life
In Unopened Original Container (at 0°C To +10°C) is 6 months