Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Technologies
- Suitable Lamp Types
LED 365 nm, LED 400 nm, UVA
Features & Benefits
- Ready-to-Use Product Features
- Special Features
compliant with RoHS Directive 2015/863/EU
Applications & Uses
- Markets
- Cure Method
- Typical Area Of Use
-40 - 150 °C
- General Curing and Processing Information
The curing time stated in the technical data was determined in the laboratory. It can vary depending on the adhesive quantity and component geometry and is therefore a reference value.Increasing or decreasing the curing temperature and / or irradiation intensity and / or irradiation time shortens or prolongs the curing time and can lead to changed physical properties.All curing or light fixation parameters depend on material thickness and absorption, adhesive layer thickness, lamp type and distance between lamp and adhesive layer.Values measured after 24 h at approx. 23 °C / 50 % r.h., unless otherwise specified.
Properties
- Typical Properties
- Processing Parameters
Value | Units | Test Method / Conditions | |
Typical Light Fixation Time Intensity 200 Mw/Cm² Led 400 Nm | 15.0 | s | — |
Typical Curing Time( +130 °C In Air Convection Oven) | 5.0 | min | — |
Typical Curing Time( +150 °C In Air Convection Oven) | 3.0 | min | — |
Processing (Typical Adhesive Application) | Needle Dispensing | — | — |
Conditioning Time (Typical) When Stored In Cold Conditions In Containers Up To 50 Ml | 1.5 | h | — |
Conditioning Time (Typical) When Stored In Cold Conditions In Containers Up To 1000 Ml | 4.0 | h | — |
Conditioning Time (Typical) When Stored In Cold Conditions In Containers Up To 10 L | 10.0 | h | — |
Processing Time (At Rt Approx. +23 °C) | 28.0 | d | — |
Color In Cured Condition In 1 Mm Layer Thickness | Yellowish | — | — |
Transparency In Cured Condition In 1 Mm Layer Thickness | Transparent | — | — |
Value | Units | Test Method / Conditions | |
Density (Liquid) | 1.14 | g/cm³ | DIN EN ISO 2811-3 |
Viscosity Liquid | Rheometer | Shear Rate: 10 1/S | 6000.0 | mPa·s | — |
Thixotropy Index (Liquid | Rheometer) | 1.5 | — | — |
Maximum Curable Layer Thickness Delo Standard 20 | White Substrate | 400 Nm | 200 Mw/Cm² | 15 S | Plus | At Approx. +23 °C | 24 H | 2.5 | mm | — |
Maximum Curable Layer Thickness Delo Standard 20 | White Substrate | 400 Nm | 200 Mw/Cm² | 30 S | Plus | At Approx. +23 °C | 24 H | min. 4 | mm | — |
Compression Shear Strength Delo Standard 5 | Glass | Fr4 | 400 Nm | 200 Mw/Cm² | 15 S | Plus | 130 °C | 10 Min | 20.0 | MPa | — |
Compression Shear Strength Delo Standard 5 | Pc | Pc | 130 °C | 10 Min | 40.0 | MPa | — |
Compression Shear Strength Delo Standard 5 | Glass | Glass | 130 °C | 10 Min | 20.0 | MPa | — |
Tensile Strength Based On | 400 Nm | 200 Mw/Cm² | 60 S | Plus | 130 °C | 10 Min | 22.0 | MPa | DIN EN ISO 527 |
Elongation At Tear Based On | 400 Nm | 200 Mw/Cm² | 60 S | Plus | 130 °C | 10 Min | 86.0 | % | DIN EN ISO 527 |
Young'S Modulus Dmta | 400 Nm | 200 Mw/Cm² | 60 S | Plus | 130 °C | 10 Min | 1000.0 | MPa | DMTA EN ISO 400 |
Shore Hardness D (400 Nm | 200 Mw/Cm² | 15 S | Plus | 130 °C | 10 Min) | 56.0 | — | DIN EN ISO 868 |
Glass Transition Temperature Dmta | 400 Nm | 200 Mw/Cm² | 60 S | Plus | 130 °C | 10 Min | 48.0 | °C | — |
Coefficient Of Linear Expansion (Delo Standard 26 | Tma | Evaluation T: 60 °C - 140 °C | 400 Nm | 200 Mw/Cm² | 15 S | Plus | 130 °C | 10 Min) | 214.0 | ppm/K | — |
Coefficient Of Linear Expansion (Delo Standard 26 | Tma | Evaluation T: -40 °C - -20 °C | 400 Nm | 200 Mw/Cm² | 15 S | Plus | 130 °C | 10 Min) | 91.0 | ppm/K | — |
Shrinkage Delo Standard 13 | 400 Nm | 200 Mw/Cm² | 15 S | Plus | 130 °C | 10 Min | 3.3 | vol. % | — |
Water Absorption Based On 400 Nm | 200 Mw/Cm² | 15 S | Plus | 130 °C | 10 Min | Type Of Storage: Media | Medium: Distilled Water | Storage Temperature: At Approx. +23 °C | Duration: 24 H | 0.5 | wt. % | DIN EN ISO 62 |
Volume Resistivity Based On 400 Nm | 200 Mw/Cm² | 15 S | Plus | 130 °C | 10 Min | min. 1xE13 | Ohm·cm | DIN EN 62631-3-1 |
Surface Resistance Based On | 400 Nm | 200 Mw/Cm² | 15 S | Plus | 130 °C | 10 Min | 6xE11 | Ohm | DIN EN 62631-3-2 |
Creep Resistance Cti Based On | 400 Nm | 200 Mw/Cm² | 60 S | Plus | 130 °C | 10 Min | 600.0 | — | DIN EN 60112 |
Regulatory & Compliance
- Certifications & Compliance
Technical Details & Test Data
- Converting Table
°F = (°C *1.8) +32
1 inch = 25.4 mm
1 mil = 25.4
1 oz = 28.3495 g
1 MPa = 145.04 psi
1 GPa = 145.04 ksi
1cP = 1 mPa•s
IN = 0.225 lb
Storage & Handling
- Storage Life
In Unopened Original Container (Up To <= 1 L at 0°C To +10°C) is 6 months
- Storage Life
In Unopened Original Container (Up To > 10 L Per Component at 0°C To +10°C) is 3 months