Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Technologies
- Suitable Lamp Types
LED 365 nm, LED 400 nm
Features & Benefits
- Ready-to-Use Product Features
- Special Features
compliant with RoHS Directive 2015/863/EU
Applications & Uses
- Markets
- Cure Method
- Typical Area Of Use
- -40 - 120 °C
- mixed bondings with plastics
- bonding of fastening elements (ONSERT®)
- General Curing and Processing Information
The curing time stated in the technical data was determined in the laboratory. It can vary depending on the adhesive quantity and component geometry and is therefore a reference value.Increasing or decreasing the curing temperature and / or irradiation intensity and / or irradiation time shortens or prolongs the curing time and can lead to changed physical properties.All curing or light fixation parameters depend on material thickness and absorption, adhesive layer thickness, lamp type and distance between lamp and adhesive layer.Values measured after 24 h at approx. 23 °C / 50 % r.h., unless otherwise specified.
Properties
- Typical Properties
- Processing Parameters
| Value | Units | Test Method / Conditions | |
| Typical Irradiation Time (Intensity 200 Mw/Cm² Led 400 Nm) | 2.0 | — | — |
| Typical Curing Time (At +130 °C In Air Convection Oven) | 2.0 | — | — |
| Conditioning Time (Typical) When Stored In Cold Conditions In Containers Up To 50 Ml | 30.0 | min | — |
| Conditioning Time (Typical) When Stored In Cold Conditions In Containers Up To 1,000 Ml | 4.0 | h | — |
| Processing Time (In Standard Climate +23 °C / 50 % R. H. In Containers Up To 50 Ml) | 14.0 | d | — |
| Processing Time (In Standard Climate +23 °C / 50 % R. H. In Containers Up To 600 Ml) | 10.0 | d | — |
| Color In Uncured Condition | Red | — | — |
| Color In Cured Condition (in 0.1 Mm Layer Thickness) | Reddish | — | — |
| Transparency In Cured Condition (in 0.1 Mm Layer Thickness) | Transparent | — | — |
| Fluorescence | Fluorescent | — | — |
| Value | Units | Test Method / Conditions | |
| Density Delo Standard 13 | Liquid | 1.08 | g/cm³ | — |
| Viscosity Liquid | Rheometer | Shear Rate: 10 1/S | Gap: 500 Μm | 23000.0 | mPa·s | — |
| Compression Shear Strength Delo Standard 5 | Glass | Al | 400 Nm | 200 Mw/Cm² | 10 S | 26.0 | MPa | — |
| Compression Shear Strength Delo Standard 5 | Glass | Fr4 | 400 Nm | 200 Mw/Cm² | 10 S | 26.0 | MPa | — |
| Compression Shear Strength Delo Standard 5 | Glass | Pa6 | 400 Nm | 200 Mw/Cm² | 10 S | 18.0 | MPa | — |
| Tensile Strength By The Criteria Of 400 Mw/Cm² | 200 Mw/Cm² | 60 S | Plus | At Approx. +23 °C | Rel. Air Humidity: 50 % | 3 H | 18.0 | MPa | Din En Iso 527 |
| Elongation At Tear By The Criteria Of 400 Mw/Cm² | 200 Mw/Cm² | 60 S | Plus | At Approx. +23 °C | Rel. Air Humidity: 50 % | 3 H | 235.0 | % | Din En Iso 527 |
| Young'S Modulus Dmta | 400 Nm | 200 Mw/Cm² | 60 S | 750.0 | MPa | — |
| Shore Hardness D By The Criteria Of Din En Iso 868 | 400 Mw/Cm² | 200 Mw/Cm² | 60 S | Plus | At Approx. +23 °C | Rel. Air Humidity: 50 % | 3 H | 50.0 | — | — |
| Glass Transition Temperature Dmta | 400 Nm | 200 Mw/Cm² | 60 S | 105.0 | °C | — |
| Coefficient Of Linear Expansion Delo Standard 26 | Tma | Evaluation T: 40 °C - 60 °C | 400 Mw/Cm² | 200 Mw/Cm² | 60 S | Plus | At Approx. +23 °C | Rel. Air Humidity: 50 % | 3 H | 175.0 | ppm/K | — |
| Shrinkage Delo Standard 13 | 400 Mw/Cm² | 200 Mw/Cm² | 60 S | 6.4 | vol. % | — |
| Water Absorption By The Criteria Of Layer Thickness: 2 Mm | 400 Mw/Cm² | 200 Mw/Cm² | 60 S | Type Of Storage: Media | Medium: Distilled Water | Storage Temperature: At Approx. +23 °C | 1.3 | % | Din En Iso 62 |
Regulatory & Compliance
- Certifications & Compliance
Technical Details & Test Data
- Converting Table
°F = (°C *1.8) +32
1 inch = 25.4 mm
1 mil = 25.4
1 oz = 28.3495 g
1 MPa = 145.04 psi
1 GPa = 145.04 ksi
1cP = 1 mPa•s
IN = 0.225 lb
Storage & Handling
- Storage Life
In Unopened Original Container (0 °C To +10 °C) is 6 months