Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Technologies
- Suitable Lamp Types
LED 365 nm, LED 400 nm
Features & Benefits
- Ready-to-Use Product Features
- Special Features
- compliant with RoHS Directive 2015/863/EU
- compliant with limits of VOC content in adhesive acc. to GB33372-2020
Applications & Uses
- Markets
- Cure Method
- Typical Area Of Use
- -40 - 150 °C
- pin sealing
- pin potting
- General Curing and Processing Information
The curing time stated in the technical data was determined in the laboratory. It can vary depending on the adhesive quantity and component geometry and is therefore a reference value.Increasing or decreasing the curing temperature and / or irradiation intensity and / or irradiation time shortens or prolongs the curing time and can lead to changed physical properties.All curing or light fixation parameters depend on material thickness and absorption, adhesive layer thickness, lamp type and distance between lamp and adhesive layer.Values measured after 24 h at approx. 23 °C / 50 % r.h., unless otherwise specified.
Properties
- Typical Properties
- Processing Parameters
| Value | Units | Test Method / Conditions | |
| Typical Irradiation Time (Intensity 200 Mw/Cm² Led 400 Nm) | 7.0 | s | — |
| Typical Irradiation Time (Intensity 1000 Mw/Cm² Led 400 Nm) | 4.0 | s | — |
| Conditioning Time (Typical) When Stored In Cold Conditions In Containers Up To 50 Ml | 30.0 | min | — |
| Conditioning Time (Typical) When Stored In Cold Conditions In Containers Up To 1,000 Ml | 4.0 | h | — |
| Processing Time (Rt Approx. +23 °C) | 30.0 | d | — |
| Color In Uncured Condition | Yellowish | — | — |
| Color In Cured Condition In 0.1 Mm Layer Thickness | Yellowish | — | — |
| Color In Cured Condition In 1 Mm Layer Thickness | Yellowish | — | — |
| Fluorescence | Fluorescent | — | — |
| Value | Units | Test Method / Conditions | |
| Density Delo Standard 13 | Liquid | 1.01 | g/cm³ | — |
| Viscosity Liquid | Viscosimeter | 2200.0 | mPa·s | — |
| Maximum Curable Layer Thickness Delo Standard 20 | 400 Nm | 200 Mw/Cm² | 60 S | 4.0 | mm | — |
| Compression Shear Strength Delo Standard 5 | Glass | Stainless Steel | 400 Nm | 200 Mw/Cm² | 60 S | Plus | At Approx. +23 °C | 72 H | Rel. Air Humidity: 50 % | 2.0 | MPa | — |
| Compression Shear Strength Delo Standard 5 | Glass | Pa6 | 400 Nm | 200 Mw/Cm² | 60 S | Plus | At Approx. +23 °C | 72 H | Rel. Air Humidity: 50 % | 2.0 | MPa | — |
| Compression Shear Strength Delo Standard 5 | Glass | Pbt | 400 Nm | 200 Mw/Cm² | 60 S | Plus | At Approx. +23 °C | 72 H | Rel. Air Humidity: 50 % | 1.0 | MPa | — |
| Tensile Strength Based On 400 Nm | 200 Mw/Cm² | 90 S | Plus | At Approx. +23 °C | 72 H | Rel. Air Humidity: 50 % | 4.0 | MPa | Din En Iso 527 |
| Elongation At Tear Based On 400 Nm | 200 Mw/Cm² | 90 S | Plus | At Approx. +23 °C | 72 H | Rel. Air Humidity: 50 % | 540.0 | % | Din En Iso 527 |
| Young'S Modulus Dmta | 400 Nm | 200 Mw/Cm² | 60 S | Plus | At Approx. +23 °C | 72 H | Rel. Air Humidity: 50 % | max. 10 | MPa | — |
| Shore Hardness A Based On 400 Nm | 200 Mw/Cm² | 90 S | Plus | At Approx. +23 °C | 72 H | Rel. Air Humidity: 50 % | 24.0 | — | Din En Iso 868 |
| Glass Transition Temperature Dmta | 400 Nm | 200 Mw/Cm² | 60 S | Plus | At Approx. +23 °C | 72 H | Rel. Air Humidity: 50 % | 10.0 | °C | — |
| Coefficient Of Linear Expansion (Delo Standard 26 | Tma | Evaluation T: -40 °C - 150 °C | 400 Nm | 200 Mw/Cm² | 60 S | Plus | at Approx. +23 °C | 72 H | Rel. Air Humidity: 50 %) | 240.0 | ppm/K | — |
| Shrinkage (Delo Standard 13 | 400 Nm | 200 Mw/Cm² | 90 S | Plus | At Approx. +23 °C | 72 H | Rel. Air Humidity: 50 %) | 5.6 | vol. % | — |
| Water Absorption (Based On Layer Thickness: 4 Mm | 400 Nm | 200 Mw/Cm² | 90 S | Plus | At Approx. +23 °C | 72 H | Rel. Air Humidity: 50 % | Type Of Storage: Media | Medium: Distilled Water | Storage Temperature: At Approx. +23 °C) | 1.1 | wt. % | Din En Iso 62 |
| Creep Resistance CTI (Based On 400 Nm | 200 Mw/Cm² | 60 S | Plus | At Approx. +23 °C | 72 H | Rel. Air Humidity: 50 %) | 600.0 | — | Din En 60112 |
Regulatory & Compliance
- Certifications & Compliance
Technical Details & Test Data
- Converting Table
°F = (°C *1.8) +32
1 inch = 25.4 mm
1 mil = 25.4
1 oz = 28.3495 g
1 MPa = 145.04 psi
1 GPa = 145.04 ksi
1cP = 1 mPa•s
IN = 0.225 lb
Storage & Handling
- Storage Life
In Unopened Original Container (0°C To +10 °C) is 6 months