Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Technologies
- Suitable Lamp Types
LED 365 nm, LED 400 nm, UVA
Features & Benefits
- Ready-to-Use Product Features
- Special Features
- compliant with RoHS Directive 2015/863/EU
- compliant with limits of VOC content in adhesive acc. to GB33372-2020
- passes ANSI/UL 94 HB Flame Test
- Function
encapsulant / potting compound
Applications & Uses
- Markets
- Cure Method
- Typical Area Of Use
-40 - 120 °C
- General Curing and Processing Information
The curing time stated in the technical data was determined in the laboratory. It can vary depending on the adhesive quantity and component geometry and is therefore a reference value.Increasing or decreasing the curing temperature and / or irradiation intensity and / or irradiation time shortens or prolongs the curing time and can lead to changed physical properties.All curing or light fixation parameters depend on material thickness and absorption, adhesive layer thickness, lamp type and distance between lamp and adhesive layer.Values measured after 24 h at approx. 23 °C / 50 % r.h., unless otherwise specified.
Properties
- Typical Properties
- Processing Parameters
| Value | Units | Test Method / Conditions | |
| Typical Irradiation Time (Intensity 55 - 60 Mw/Cm² Uva) | 10.0 | s | — |
| Typical Irradiation Time (Intensity 200 Mw/Cm² Led 400 Nm) | 4.0 | s | — |
| Typical Irradiation Time (Intensity 1000 Mw/Cm² Led 400 Nm) | 3.0 | s | — |
| Conditioning Time (Typical) When Stored In Cold Conditions In Containers Up To 50 Ml | 30.0 | min | — |
| Conditioning Time (Typical) When Stored In Cold Conditions In Containers Up To 1,000 Ml | 4.0 | h | — |
| Processing Time (Rt Approx. +23 °C) | 30.0 | d | — |
| Transparency | Transparent | — | — |
| Color In Cured Condition In 0.1 Mm Layer Thickness | Colorless | — | — |
| Value | Units | Test Method / Conditions | |
| Density Delo Standard 13 | Liquid | 1.01 | g/cm³ | — |
| Viscosity Liquid | Rheometer | Shear Rate: 2 1/S | Gap: 500 Μm | 2100.0 | mPa·s | — |
| Viscosity Liquid | Rheometer | Shear Rate: 10 1/S | Gap: 500 Μm | 2100.0 | mPa·s | — |
| Compression Shear Strength Delo Standard 5 | Glass | Al | 60 Mw/Cm² | 60 S | Plus | At Approx. +23 °C | 24 H | 6.0 | MPa | — |
| Compression Shear Strength Delo Standard 5 | Glass | Fr4 | 60 Mw/Cm² | 60 S | Plus | At Approx. +23 °C | 24 H | 9.0 | MPa | — |
| Compression Shear Strength Delo Standard 5 | Glass | Glass | 60 Mw/Cm² | 60 S | Plus | At Approx. +23 °C | 24 H | 7.0 | MPa | — |
| Compression Shear Strength Delo Standard 5 | Glass | Pa6 | 60 Mw/Cm² | 60 S | Plus | At Approx. +23 °C | 24 H | 6.0 | MPa | — |
| Compression Shear Strength Delo Standard 5 | Glass | Pbt | 60 Mw/Cm² | 60 S | Plus | At Approx. +23 °C | 24 H | 2.0 | MPa | — |
| Tensile Strength By The Criteria Of 60 Mw/Cm² | 90 S | Plus | At Approx. +23 °C | 24 H | 6.0 | MPa | Din En Iso 527 |
| Elongation At Tear By The Criteria Of 60 Mw/Cm² | 90 S | Plus | At Approx. +23 °C | 24 H | 315.0 | % | Din En Iso 527 |
| Young'S Modulus By The Criteria Of 60 Mw/Cm² | 90 S | Plus | At Approx. +23 °C | 24 H | 17.0 | MPa | Din En Iso 527 |
| Shore Hardness A By The Criteria Of 60 Mw/Cm² | 90 S | Plus | At Approx. +23 °C | 24 H4 | 60.0 | — | Din En Iso 868 |
| Glass Transition Temperature Delo Standard 24 | Rheometer | 60 Mw/Cm² | Plus | 70.0 | °C | — |
| Shrinkage Delo Standard 13 | 60 Mw/Cm² | 90 S | 5.4 | vol. % | — |
| Creep Resistance Cti By The Criteria Of Vde 0303-11 | 60 Mw/Cm² | 90 S | 600.0 | — | — |
Regulatory & Compliance
- Certifications & Compliance
Technical Details & Test Data
- Converting Table
°F = (°C *1.8) +32
1 inch = 25.4 mm
1 mil = 25.4
1 oz = 28.3495 g
1 MPa = 145.04 psi
1 GPa = 145.04 ksi
1cP = 1 mPa•s
IN = 0.225 lb- Parameters
Storage & Handling
- Storage Life
In Unopened Original Container (0°C To +10 °C) is 6 months