Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Product Type
- Technologies
Features & Benefits
- Special Features
- compliant with RoHS Directive 2015/863/EU
- tested for biocompatibility and meets the requirements according to DIN EN ISO 10993-5: test for cytotoxicity
- passes ANSI/UL 94 HB Flame Test
- Component B is humidity-sensitive
- Function
- -40 - 125 °C
- metal bondings
- mixed bondings with plastics
Applications & Uses
- Markets
- Cure Method
- Typical Area Of Use
- -40 - 150 °C
- pin sealing
- General Curing and Processing Information
The curing time stated in the technical data was determined in the laboratory. It can vary depending on the adhesive quantity and component geometry and is therefore a reference value.Unless otherwise specified, the values were measured after 168 h at approx. 23 °C / 50 % r. h., and the values of heat-cured samples were measured after 24 h at approx. 23 °C / 50 % r. h.
Properties
- Typical Properties
- Processing Parameters
Value | Units | Test Method / Conditions | |
Until Initial Strength At Rt Approx. +23 °C Tensile Shear Strength 1 - 2 Mpa | 90.0 | min | — |
Until Functional Strength At Rt Approx. +23 °C Tensile Shear Strength > 10 Mpa | 6.0 | h | — |
Until Final Strength At Rt Approx. +23 °C | 72.0 | h | — |
Until Functional Strength At +80 °C Tensile Shear Strength > 10 Mpa | 20.0 | min | — |
Until Final Strength At +80 °Counts | 22.0 | min | — |
Processing Mixing Ratio A : B - Volume | 1 : 1 | — | — |
Processing Mixing Ratio A : B - Weight | 1 : 1 | — | — |
Processing Time After Mixing In 3 G Batch At Rt Approx. +23 °C | 10.0 | min | — |
Color In Cured Condition In 1 Mm Layer Thickness | Black | — | — |
Transparency In Cured Condition In 1 Mm Layer Thickness | Opaque | — | — |
Filler Particle Type | Minerals | — | — |
Value | Units | Test Method / Conditions | |
Density (Delo Standard 13 | Liquid) | 1.45 | g/cm³ | — |
Viscosity Component A | Liquid | Viscosimeter | 80000.0 | mPa·s | — |
Viscosity Component B | Liquid | Viscosimeter | 80000.0 | mPa·s | — |
Tensile Shear Strength Al | Al | Pretreatment: Sand-Blasted | At Approx. +23 °C | 7 D | Measuring Temperature: 100 °C | 2.5 | MPa | DIN EN 1465 |
Tensile Shear Strength Al | Al | Pretreatment: Sand-Blasted | At Approx. +23 °C | 24 H | 12.0 | MPa | DIN EN 1465 |
Tensile Shear Strength Al | Al | Pretreatment: Sand-Blasted | At Approx. +23 °C | 72 H | 13.0 | MPa | DIN EN 1465 |
Tensile Shear Strength By The Criteria Of | Al | Al | Pretreatment: Sand-Blasted | At Approx. +23 °C | 168 H | 16.0 | MPa | DIN EN 1465 |
Peel Resistance Delo Standard 38 | Steel | Steel | Pretreatment: Sand-Blasted | At Approx. +23 °C | 7 D | 6.0 | N/mm | — |
Tensile Strength (Approx. +23 °C | 7 D) | 13.0 | MPa | DIN EN ISO 527 |
Elongation At Tear | At Approx. +23 °C | 7 D | 20.0 | % | DIN EN ISO 527 |
Young'S Modulus By The Criteria Of Approx. +23 °C | 7 D | 500.0 | MPa | DIN EN ISO 527 |
Shore Hardness D (At Approx. +23 °C | 7 D) | 69.0 | — | DIN EN ISO 868 |
Glass Transition Temperature Delo Standard 24 | Rheometer | 49.0 | °C | — |
Coefficient Of Linear Expansion (Delo Standard 26 | Tma | Evaluation T: 25 °C - 140 °C) | 162.0 | ppm/K | — |
Water Absorption By The Criteria Of Layer Thickness: 4 Mm | Type Of Storage: Media | Medium: Distilled Water | Storage Temperature: At Approx. +23 °C | Duration: 24 H | 0.24 | wt. % | DIN EN ISO 62 |
Decomposition Temperature Delo Standard 36 | 225.0 | °C | — |
Volume Resistivity | min. 1xE13 | Ohm·cm | — |
Surface Resistance Din En 62631-3-2 | min. 1xE13 | Ohm | DIN EN 62631-3-2 |
Dielectric Strength | 16.6 | kV/mm | DIN EN 60243-1 |
Creep Resistance Cti M | 600.0 | — | DIN EN 60112 |
Regulatory & Compliance
- Certifications & Compliance
Technical Details & Test Data
- Converting Table
°F = (°C *1.8) +32
1 inch = 25.4 mm
1 mil = 25.4
1 oz = 28.3495 g
1 MPa = 145.04 psi
1 GPa = 145.04 ksi
1cP = 1 mPa•s
IN = 0.225 lb- Parameters
Storage & Handling
- Storage Life
In Unopened Original Container (at +15 °C To +30 °C is 6 months