Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Product Type
- Technologies
Features & Benefits
- Special Features
- compliant with RoHS Directive 2015/863/EU
- UL listing: UL file E467212 (Yellow Card)
- tested for biocompatibility and meets the requirements according to DIN EN ISO 10993-5: test for cytotoxicity
- compliant with limits of VOC content in adhesive acc. to GB33372-2020
- passes ANSI/UL 94 HB Flame Test
- Component B is humidity-sensitive
Applications & Uses
- Markets
- Cure Method
- Typical Area Of Use
- -40 - 125 °C
- glass/metal bondings
- mixed bondings with plastics
- General Curing and Processing Information
The curing time stated in the technical data was determined in the laboratory. It can vary depending on the adhesive quantity and component geometry and is therefore a reference value.Unless otherwise specified, the values were measured after 168 h at approx. 23 °C / 50 % r. h., and the values of heat-cured samples were measured after 24 h at approx. 23 °C / 50 % r. h.
Properties
- Typical Properties
- Processing Parameters
| Value | Units | Test Method / Conditions | |
| Until Initial Strength (Rt Approx. +23 °C Tensile Shear Strength 1 - 2 Mpa) | 5.5 | h | — |
| Until Functional Strength (Rt Approx. +23 °C Tensile Shear Strength > 10 Mpa) | 24.0 | h | — |
| Until Final Strength (Rt Approx. +23 °C) | 72.0 | h | — |
| Until Initial Strength (+80 °C Tensile Shear Strength 1 - 2 Mpa) | 25.0 | min | — |
| Until Functional Strength (+80 °C Tensile Shear Strength > 10 Mpa) | 60.0 | min | — |
| Until Final Strength (+80 °C) | 90.0 | min | — |
| Processing Mixing Ratio A : B - Volume | 1 : 1 | — | — |
| Processing Mixing Ratio A : B - Weight | 1 : 1 | — | — |
| Processing Time (After Mixing In 100 G Batch At Rt Approx. +23 °C) | 30.0 | min | — |
| Reaction Temperature (Max.) In 100 G Batch | 35.0 | °C | — |
| Color In Cured Condition In 1 Mm Layer Thickness | Beige | — | — |
| Filler Particle Type | Minerals | — | — |
| Value | Units | Test Method / Conditions | |
| Density Of Component A | 1.48 | g/cm³ | — |
| Density Of Component B | 1.44 | g/cm³ | — |
| Tensile Shear Strength Based On Din En 1465 | Al | Al | Pretreatment: Sand-Blasted | At Approx. +23 °C | 7 D | Measuring Temperature: 100 °C | 3.0 | MPa | — |
| Tensile Shear Strength Based On Din En 1465 | Al | Al | Pretreatment: Sand-Blasted | At Approx. +23 °C | 168 H | 16.0 | MPa | — |
| Peel Resistance Delo Standard 38 | Steel | Steel | Pretreatment: Sand-Blasted | At Approx. +23 °C | 7 D | 10.0 | N/mm | — |
| Tensile Strength Based On Din En Iso 527 | At Approx. +23 °C | 7 D | 10.0 | MPa | — |
| Elongation At Tear Based On Din En Iso 527 | At Approx. +23 °C | 7 D | 70.0 | % | — |
| Young'S Modulus Based On Din En Iso 527 | At Approx. +23 °C | 7 D | 100.0 | MPa | — |
| Shore Hardness A Based On Din En Iso 868 | At Approx. +23 °C | 7 D | 90.0 | — | — |
| Shore Hardness D Based On Din En Iso 868 | At Approx. +23 °C | 7 D | 50.0 | — | — |
| Coefficient Of Linear Expansion Delo Standard 26 | Tma | Evaluation T: 30 °C - 140 °C | 205.0 | ppm/K | — |
| Water Absorption Based On Din En Iso 62 | Type Of Storage: Media | Medium: Distilled Water | Storage Temperature: At Approx. +23 °C | Duration: 24 H | 0.3 | wt. % | — |
| Decomposition Temperature Delo Standard 36 | Type Of Storage: Temp. | Storage Temperature: 100 °C | Duration: 24 H | 221.0 | °C | — |
| Volume Resistivity Based On Vde 0303-30 | min. 1xE13 | Ohm·cm | — |
| Surface Resistance Based On Din En 62631-3-2 | min. 1xE12 | Ohm | — |
| Dielectric Strength | 17.6 | kV/mm | Din En 60243-1 |
| Creep Resistance CTI M | 600.0 | — | Din En 60112 |
Regulatory & Compliance
- Certifications & Compliance
Technical Details & Test Data
- Converting Table
°F = (°C *1.8) +32
1 inch = 25.4 mm
1 mil = 25.4
1 oz = 28.3495 g
1 MPa = 145.04 psi
1 GPa = 145.04 ksi
1cP = 1 mPa•s
IN = 0.225 lb- Parameters
Storage & Handling
- Storage Life
In Unopened Original Container (at +15 °C To +30 °C) is 6 months