| Value | Units | Test Method / Conditions | |
| Tensile Modulus (1 mm/min) | 13800 / 12800 | MPa | ISO 527 |
| Tensile Stress at Break (5 mm/min) | 230 / 200 | MPa | ISO 527 |
| Tensile Strain at Break (5 mm/min) | 3.0 / 3.0 | % | ISO 527 |
| Flexural Strength (2 mm/min) | 360 / - | MPa | ISO 178 |
| Flexural Modulus (2 mm/min) | 12500 / - | MPa | ISO 178 |
| Charpy Notched Impact Strength (+23 °C) | 13 / 13 | kJ/m2 | ISO 179/1eA |
| Charpy Unnotched Impact Strength (+23 °C) | 125 / 115 | kJ/m2 | ISO 179/1eU |
| Value | Units | Test Method / Conditions | |
| Molding Shrinkage - Parallel (72 hrs, 23°C, 50% RH) | 0 | % | ISO 294-4 / 2577 |
| Molding Shrinkage - Transverse (72 hrs, 23°C, 50% RH) | 1 | % | ISO 294-4 / 2577 |
| Moisture Absorption (T=23°C / 50%RH) | 1.5 | % | ISO 62 |
| Water Absorption (T=23°C / sat.) | 4.5 | % | ISO 62 |
| Value | Units | Test Method / Conditions | |
| Heat Deflection Temperature - HDT/A (1.80 MPa) | 235 | °C | ISO 75 |
| Melting Point (DSC) | 262 | °C | ISO 11357-1 |
| Value | Units | Test Method / Conditions | |
| Drying Time (with dew point of dried air < -30 °C) | 2.0 - 4.0 | h | — |
| Recommended Melt Temperature | 280 - 305 | °C | — |
| Recommended Mold Temperature | 70 - 100 | °C | — |
| Drying Temperature | 75 - 85 | °C | — |