Value | Units | Test Method / Conditions | |
Tensile Modulus (1 mm/min) | 18000 / 17000 | MPa | ISO 527 |
Tensile Stress at Break (5 mm/min) | 260 / 240 | MPa | ISO 527 |
Tensile Strain at Break (5 mm/min) | 3.0 / 3.0 | % | ISO 527 |
Flexural Strength (2 mm/min) | 400 / 350 | MPa | ISO 178 |
Flexural Modulus (2 mm/min) | 16500 / 15000 | MPa | ISO 178 |
Charpy Notched Impact Strength (+23 °C) | 16 / 16 | kJ/m2 | ISO 179/1eA |
Charpy Notched Impact Strength (-30°C) | 14 / 14 | kJ/m2 | ISO 179/1eA |
Charpy Unnotched Impact Strength (+23 °C) | 110 / 105 | kJ/m2 | ISO 179/1eU |
Charpy Unnotched Impact Strength (-30°C) | 85 / 85 | kJ/m2 | ISO 179/1eU |
Value | Units | Test Method / Conditions | |
Molding Shrinkage - Parallel (72 hrs, 23°C, 50% RH) | 0.1 - 0.3 | % | ISO 294-4 / 2577 |
Molding Shrinkage - Transverse (72 hrs, 23°C, 50% RH) | 0.3 - 0.5 | % | ISO 294-4 / 2577 |
Moisture Absorption (T=23°C / 50%RH) | 1.4 | % | ISO 62 |
Value | Units | Test Method / Conditions | |
Heat Deflection Temperature - HDT/A (1.80 MPa) | 240 | °C | ISO 75 |
Heat Deflection Temperature - HDT/B (0.45 MPa) | 250 | °C | ISO 75-1/-2 |
Melting Point (DSC) | 262 | °C | ISO 11357-1 |
Vicat Softening Temperature (50°C/h - 50N) | 235 | °C | ISO 306 |
Value | Units | Test Method / Conditions | |
Drying Time (with dew point of dried air < -30 °C) | 2.0 - 4.0 | h | — |
Recommended Melt Temperature | 280 - 305 | °C | — |
Recommended Mold Temperature | 70 - 100 | °C | — |
Drying Temperature | 75 - 85 | °C | — |