Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
Applications & Uses
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Filler
- Glass Fiber
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Processing Parameters
Value | Units | Test Method / Conditions | |
Tensile Modulus (1 mm/min) | 18000 / 17000 | MPa | ISO 527 |
Tensile Stress at Break (5 mm/min) | 265 / 235 | MPa | ISO 527 |
Tensile Strain at Break (5 mm/min) | 2.6 / 2.6 | % | ISO 527 |
Flexural Strength (2 mm/min) | 420 / - | MPa | ISO 178 |
Flexural Modulus (2 mm/min) | 16000 / - | MPa | ISO 178 |
Charpy Notched Impact Strength (+23 °C) | 18 / 17 | kJ/m2 | ISO 179/1eA |
Charpy Unnotched Impact Strength (+23 °C) | 105 / 100 | kJ/m2 | ISO 179/1eU |
Value | Units | Test Method / Conditions | |
Moisture Absorption (T=23°C / 50%RH) | 1.4 | % | ISO 62 |
Value | Units | Test Method / Conditions | |
Heat Deflection Temperature - HDT/A (1.80 MPa) | 245 | °C | ISO 75 |
Melting Point (DSC) | 262 | °C | ISO 11357-1 |
Value | Units | Test Method / Conditions | |
Drying Time (with dew point of dried air < -30 °C) | 2.0 - 4.0 | h | — |
Recommended Melt Temperature | 280 - 305 | °C | — |
Recommended Mold Temperature | 70 - 100 | °C | — |
Drying Temperature | 75 - 85 | °C | — |