Value | Units | Test Method / Conditions | |
Tensile Modulus (1 mm/min) | 6000 | MPa | ISO 527 |
Tensile Stress at Yield (5 mm/min) | 80 | MPa | ISO 527 |
Tensile Strain at Break (5 mm/min) | 3 | % | ISO 527 |
Charpy Notched Impact Strength (+23 °C) | 7 | kJ/m2 | ISO 179/1eA |
Charpy Unnotched Impact Strength (+23 °C) | 70 | kJ/m2 | ISO 179/1eU |
Value | Units | Test Method / Conditions | |
Melt Flow Rate - MFR (230 °C/2.16 kg) | 2 | g/10 min | ISO 1133 |
Molding Shrinkage - Parallel (72 hrs, 23°C, 50% RH) | 0.40 - 0.60 | % | ISO 294-4 / 2577 |
Molding Shrinkage - Transverse (72 hrs, 23°C, 50% RH) | 0.60 - 0.80 | % | ISO 294-4 / 2577 |
Value | Units | Test Method / Conditions | |
Heat Deflection Temperature - HDT/A (1.80 MPa) | 145 | °C | ISO 75 |
Heat Deflection Temperature - HDT/B (0.45 MPa) | 155 | °C | ISO 75 |
Vicat Softening Temperature (50°C/h - 50N) | 130 | °C | ISO 306 |
Value | Units | Test Method / Conditions | |
Recommended Melt Temperature | 200 - 280 | °C | — |
Recommended Mold Temperature | 20 - 60 | °C | — |