Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
Applications & Uses
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Color
- Flame Rating
- Flame Rating
- UL 94 HB
- Filler
- Carbon Fiber
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Flammability
- Processing Parameters
Value | Units | Test Method / Conditions | |
Tensile Modulus (1 mm/min) | 15000 / 9000 | MPa | ISO 527 |
Tensile Stress at Break (5 mm/min) | 210 / 150 | MPa | ISO 527 |
Tensile Strain at Break (5 mm/min) | 3.1 / 4.5 | % | ISO 527 |
Flexural Strength (2 mm/min) | 270 / 200 | MPa | ISO 178 |
Flexural Modulus (2 mm/min) | 12500 / 9000 | MPa | ISO 178 |
Charpy Notched Impact Strength (+23 °C) | 5.5 / 7 | kJ/m2 | ISO 179/1eA |
Charpy Unnotched Impact Strength (+23 °C) | 45 / 55 | kJ/m2 | ISO 179/1eU |
Value | Units | Test Method / Conditions | |
Molding Shrinkage - Parallel (72 hrs, 23°C, 50% RH) | 0.20 - 0.40 | % | ISO 294-4 / 2577 |
Molding Shrinkage - Transverse (72 hrs, 23°C, 50% RH) | 0.60 - 0.90 | % | ISO 294-4 / 2577 |
Value | Units | Test Method / Conditions | |
Heat Deflection Temperature - HDT/A (1.80 MPa) | 245 | °C | ISO 75 |
Melting Point (DSC) | 262 | °C | ISO 11357-1 |
Value | Units | Test Method / Conditions | |
Flammability (0.8 mm) | HB | — | UL 94 |
Value | Units | Test Method / Conditions | |
Drying Time (with dew point of dried air < -30 °C) | 2.0 - 4.0 | h | — |
Recommended Melt Temperature | 270 - 300 | °C | — |
Recommended Mold Temperature | 80 - 110 | °C | — |
Drying Temperature | 75 - 85 | °C | — |
Regulatory & Compliance
- Certifications & Compliance
Packaging & Availability
- Regional Availability
- Regional availability
- Europe