Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
Applications & Uses
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Color
- Flame Rating
- Physical Form
- Flame Rating
- UL 94 HB
- Filler
- Glass Fiber
- Mechanical Properties
- Thermal Properties
- Flammability
- Processing Parameters
Value | Units | Test Method / Conditions | |
Tensile Modulus (1 mm/min) | 5500 | MPa | ISO 527 |
Tensile Stress at Break (5 mm/min) | 100 | MPa | ISO 527-2/1A |
Tensile Strain at Break (5 mm/min) | 3 | % | ISO 527 |
Izod Notched Impact Strength (+23 °C) | 5 | kJ/m2 | ISO 180/1A |
Value | Units | Test Method / Conditions | |
Heat Deflection Temperature - HDT/A (1.80 MPa) | 250 | °C | ISO 75 |
Melting Point (DSC) | 262 | °C | ISO 11357-1 |
Vicat Softening Temperature (50°C/h - 50N) | 240 | °C | ISO 306 |
Value | Units | Test Method / Conditions | |
Flammability (0.8 mm) | HB | — | UL 94 |
Value | Units | Test Method / Conditions | |
Drying Time (with dew point of dried air < -30 °C) | 2.0 - 4.0 | h | — |
Recommended Melt Temperature | 260 - 285 | °C | — |
Recommended Mold Temperature | 80 - 120 | °C | — |
Drying Temperature | 75 - 85 | °C | — |