Value | Units | Test Method / Conditions | |
Tensile Modulus (1 mm/min) | 14000 | MPa | ISO 527 |
Tensile Stress at Break (5 mm/min) | 235 | MPa | ISO 527 |
Flexural Strength (2 mm/min) | 340 | MPa | ISO 178 |
Flexural Modulus (2 mm/min) | 13000 | MPa | ISO 178 |
Charpy Notched Impact Strength (+23 °C) | 11 | kJ/m2 | ISO 179/1eA |
Charpy Unnotched Impact Strength (+23 °C) | 70 | kJ/m2 | ISO 179/1eU |
Value | Units | Test Method / Conditions | |
Melt Volume Rate - MVR (330 °C/2.16 kg) | 11 | cm3/10 min | ISO 1133 |
Value | Units | Test Method / Conditions | |
Heat Deflection Temperature - HDT/A (1.80 MPa) | 280 | °C | ISO 75 |
Melting Point (DSC) | 310 | °C | ISO 11357-1 |
Value | Units | Test Method / Conditions | |
Drying Time | 4.0 - 6.0 | h | - |
Recommended Melt Temperature | 325 - 345 | °C | - |
Recommended Mold Temperature | 135 - 165 | °C | - |
Drying Temperature | 90 - 110 | °C | - |