All information, including illustrations, is believed to be reliable. Users, however, should independently evaluate the suitability of each product for their application. Dr. D. Müller GmbH makes no warranties as to the accuracy or completeness of the information, and disclaims any liability regarding its use. Dr. D. Müller GmbH only obligations are those in the Standard Terms and Conditions of Sale for this product and in no case will Dr. D. Müller GmbH be liable for any incidental, indirect or consequential damages arising from the sale, resale, use, or misuse of the product. Dr. D. Müller GmbH Specifications are subject to change without notice. In addition, Dr. D. Müller GmbH reserves the right to make changes in materials or processing without notification to the Buyer, which do not affect compliance with any applicable specification.
Applications & Uses
- Applications
- Applications
Structure: Flexiso® FI 13014 is a milky, turbid, highly rugged polyester film. This film has good machine running properties, high dimensional stability and good flatness.
Properties
- Physical Form
- Mechanical Properties
- Typical Properties
| Value | Units | Test Method / Conditions | |
| Dielectric Strength | 22 | kV | ASTM-D-149 |
| Elongation at Break MD | 131 | % | ASTM-D-882 |
| Elongation at Break MD | 173 | % | ASTM-D-882 |
| Elongation at Break MD | 183 | % | ASTM-D-882 |
| Elongation at Break TD | 103 | % | ASTM-D-882 |
| Elongation at Break TD | 113 | % | ASTM-D-882 |
| Elongation at Break TD | 116 | % | ASTM-D-882 |
| Roughness Ra | 41 | nm | Intern |
| Roughness Ra | 28 | nm | Intern |
| Roughness Ra | 46 | nm | Intern |
| Roughness Rz | 532 | nm | Intern |
| Roughness Rz | 636 | nm | Intern |
| Roughness Rz | 866 | nm | Intern |
| Tensile Strength MD | 21 | daN/mm² | ASTM-D-882 |
| Tensile Strength MD | 20 | daN/mm² | ASTM-D-882 |
| Tensile Strength MD | 19 | daN/mm² | ASTM-D-882 |
| Tensile Strength TD | 24 | daN/mm² | ASTM-D-882 |
| Tensile Strength TD | 22 | daN/mm² | ASTM-D-882 |
| Value | Units | Test Method / Conditions | |
| Light Transmission | 51 | % | ASTM-D-1003 |
| Light Transmission | 40 | % | ASTM-D-1003 |
| Shrinkage (150°C for 30 min., MD) | 1.8 | % | Intern |
| Shrinkage (150°C for 30 min., MD) | 1.4 | % | Intern |
| Shrinkage (150°C for 30 min., Td) | 0.6 | % | Intern |
| Shrinkage (150°C for 30 min., Td) | 0.5 | % | Intern |
| Shrinkage (150°C for 30 min., Td) | 0.4 | % | Intern |
| Thickness | 125 | — | — |
| Thickness | 190 | — | — |
| Thickness | 250 | — | — |
| Volume Resistance | 3x1018 | Ω.cm | ASTM-D-257 |
| Yield | 5.7 | m²/kg | Intern |
| Yield | 3.8 | m²/kg | Intern |
| Yield | 2.85 | m²/kg | Intern |