Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Core Type
- Composite Materials Functions
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
Applications & Uses
- Markets
- Applications
- Composites End Use
- Plastics & Elastomers End Uses
- Blowing Agents
HFCs/CFCs/HCFCs-free
Properties
- Typical Properties
| Value | Units | Test Method / Conditions | |
| Nominal Density | 490 | kg/m³ | ASTM D1622/EN 1602/EN ISO 845 |
| Compressive Strength (Parallel,23°C) | 16.4 | Mpa | ASTM D1621/EN 826 |
| Compressive Strength (Perpendicular,Weakest Direction,23°C) | 16 | Mpa | ASTM D1621/EN 826 |
| Compressive Modulus (Parallel,23°C) | 440 | Mpa | ASTM D1621/EN 826 |
| Compressive Modulus (Perpendicular,Weakest Direction,23°C) | 375 | Mpa | ASTM D1621/EN 826 |
| Compressive Strength (Parallel,-165°C) | 47 | Mpa | ASTM D1621/EN 826 |
| Compressive Strength (Perpendicular,Weakest Direction,-165°C) | 47 | Mpa | ASTM D1621/EN 826 |
| Flexural Strength (Parallel, Met.I,23°C) | 22.5 | Mpa | ASTM C203/EN 12089 |
| Flexural Modulus (Parallel, Met.I,23°C) | 620 | Mpa | ASTM C203/EN 12089 |
| Max. Flexural Strain (Met.I,23°C) | 0.06 | Length | ASTM C203/EN 12089 |
| Heat Distortion Temperature, Met.A | 58 - 63 | °C | ASTM D648/EN ISO 75 |
| Tensile Strength (Parallel, Met.I,23°C) | 11.4 | Mpa | ASTM D1623-A/EN 1607 |
| Tensile Strength (Perpendicular,Weakest Direction,23°C) | 11.2 | Mpa | ASTM D1623-A/EN 1607 |
| Tensile E-modulus (All directions,-165°C) | 110 | Mpa | ASTM D1623-A/EN 1607 |
| Thermal Conductivity (Initial ,10°C) | 72 | mW/mK | ASTM C518/ASTM C177/EN 12667 |
| Thermal Conductivity (180 Days 10°C,25 Mm Thickness Sample Aged 180 Days At 23°C, 50% R.H.) | 74 | mW/mK | ASTM C518/ASTM C177/EN 12667 |
| Coefficient Of Thermal Stress Resistance (-265°F/74°F, -165°C/+23°C) | min. 5 | — | CINI 2.7.01 |
| Poisson's Ratio (165°C) | 0.4 | — | ASTM D1623/EN 1607 |
| Poisson's Ratio (23°C) | 0.55 - 0.6 | — | ASTM D1623/EN 1607 |
| Coefficient Of Linear Thermal Expansion (-321°F/+74°F,-196°C/+23°C) | 45 | 1/K·10E-6 | ASTM D696/EN 13471 |
| Coefficient of linear thermal expansion CTE (+70/+120°F/ +21/+48°C) | 50 | 1/K·10E-6 | ASTM D696/EN 13471 |
| Fire Reaction | B3 | Class | DIN 4102 |
| Leachable Chlorides | max. 60 | ppm | ASTM C871/EN 13468 |
| Dimensional Stability (48H,-13°F/-25°C,Length/Width,Thickness) | ±0.5 ±0.5 | % | ASTM D2126/EN 1604 |
| Dimensional Stability (48H, 131°F/55°C,Amb.R.H.,Length/Width,Thickness) | ±0.5 ±0.5 | % | ASTM D2126/EN 1604 |
| Dimensional Stability (48H,158°F/70°C, Amb. R.H.,Length/Width,Thickness) | ±0.5 ±0.5 | % | ASTM D2126/EN 1604 |
| Water Absorption By Volume | max. 0.4 | % | ASTM D2842/EN 12087/ISO 2896 |
| Hardness | 52 | Shore D | ASTM D2240/EN ISO 868 |
| Operating Temperature | -2.5 | °C | — |
| R-Value (180 Days,1 Inch,24°C) | 2 | hr·ft²·°F/BTU | ASTM C518/EN 12667 |
| Closed-Cell Content | max. 95 | % | ASTM D6226/EN ISO 4590 |
| Ozone Depletion Potential (ODP) | 0 | — | — |
| Global warming potential (GWP) | max. 10 | — | — |
Storage & Handling
- Handling Notice
Terms "parallel" and "perpendicular" are referred to slab/specimen/block thickness direction. In some applications polyurethane may present fire risks, e.g. if exposed to fire or to excessive heat in presence of oxygen or air, including when welding or cutting with torches. It is the Customer's responsibility to determine if product described herein is appropriate for Customer's purposes and end-use and to ensure that working place, storage and disposal practices are in compliance with any applicable law