Low Voltage FR Polyolefin Insulation
Features & Benefits
- Labeling Claims
Applications & Uses
- Applications
- Cure Method
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
- Applications
- AquaGraft® 2-5150 is designed for use in a variety of 125°C automotive cable applications. These two components, when blended in a 70% EPMC-2/30% FMB-5150 blend ratio, will yield a finished compound which will allow the cable to pass various industry recognized requirements and be suitable for flame retardant 125oC applications.
- Applications
Appliance, Automotive, Battery, Welding
Properties
- Mechanical Properties
- Thermal Properties
Value | Units | Test Method / Conditions | |
Hot Creep Elongation | 25 | % | — |
Specific Gravity | 1.05 | g/cm³ | — |
Tensile Strength | 1800 | psi | — |
Value | Units | Test Method / Conditions | |
Retained Elongation (7 Days in 180°C Air Oven) | 100 | % | — |
Retained Tensile (7 Days in 180°C Air Oven) | 100 | % | — |
Regulatory & Compliance
- Certifications & Compliance
- Chemical Inventories
- Quality Standards
- Specifications
When extruded and cured consistent with standard safe wire and cable industry practices, cable insulated with the correct component ratios will comply with the requirements as specified in the following standards:
ISO 6722
SAE J1127
FT-2 Flame Rating, UL Horizontal Flame- Certification
- Certified Test Results including physical test data are included with each shipment.
Technical Details & Test Data
- Processing
AquaGraft® 2-5150 is engineered for processing on conventional thermoplastic extrusion equipment. It is recommended that these products be processed using a greater than 20:1 extruder with a high shear screw with adequate mixing sections. The compound supplied is in the cleanest state and is of the highest quality; however, the use of a breaker plate with a screen pack of approximately 20/40 mesh is recommended for optimal rheological flow and steady back pressure. Pre-heating of the conductor is recommended depending on cable construction and specific processing conditions.
Pre-drying of the FMB-5150 is generally recommended prior to use for 4 hrs. at 120˚F. When extruded in proper ratios, this system will cure with exposure to moisture at ambient temperatures, however, accelerated cure rates may be achieved with exposure of extruded cable to water bath or steam sauna. Cure rates are dependent on cable wall thickness and as such adequate cure times may differ based on cable constructions.
The following conditions are given as a guide for processingTemperature Profile
°F
ºC
Zone 1 (feed):
260-280
127-138
Zone 2:
260-280
127-138
Zone 3:
260-280
127-138
Zone 4:
260-280
127-138
Crosshead:
280-300
138-149
Die:
280-300
138-149
Packaging & Availability
- Packaging
- 2200 pounds (997.9 Kg) per box
- 200 pounds (90.7 Kg) per fiber drum
- PE Liners
- Use within 12 months of manufacturing date
Storage & Handling
- Storage
- A high level of care in storage to minimize exposure to moisture is recommended to ensure that there is no degradation of the EPMC-2. Once opened, EPMC-2 should be consumed immediately to avoid any premature gelling due to environmental moisture.
- Handling
- To ensure health and safety, Material Safety Data Sheets (MSDS) are available and should be consulted prior to use.