Down-Hole Pump Cable EPR Insulation
Features & Benefits
- Labeling Claims
Applications & Uses
- Applications
- Cure Method
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
- Applications
- Cables insulated with SUPEROHM® 2575 are designed to meet demanding performances for downhole oil well pumps operating under extremely harsh conditions. This compound may also be used as a cable jacket in appropriate applications and cable designs.
- Applications
Down-Hole Oil Pump
Properties
- Color
- Mechanical Properties
- Thermal Properties
- Electrical Properties
Value | Units | Test Method / Conditions | |
Elongation | 90 | % | — |
Specific Gravity | 1.18 | — | — |
Tensile Strength | 2700 | psi | — |
Value | Units | Test Method / Conditions | |
Retained Elongation (7 days in 121°C air oven) | 98 | % | — |
Retained Elongation (7 days in 150°C air oven) | 60 | % | — |
Retained Elongation (902 Oil Immersion - 168 hours at 150°C) | 94 | % | — |
Retained Tensile (7 days in 121°C air oven) | 104 | % | — |
Retained Tensile (7 days in 150°C air oven) | 70 | % | — |
Retained Tensile (902 Oil Immersion 168 Hours at 150°C) | 70 | % | — |
Value | Units | Test Method / Conditions | |
Dielectric Constant | 2.25 | — | — |
Dissipation Factor | 0.31 | — | — |
Volume Resistivity (204°C) | 7.50E+12 | Ohm-cm | — |
Volume Resistivity | 2.4E+16 | Ohm-cm | — |
Regulatory & Compliance
- Chemical Inventories
- Quality Standards
- Certification
- Certified Test Results including physical test data are included with each shipment.
Technical Details & Test Data
- Processing
SUPEROHM 2595 compound is engineered to be processed on conventional extrusion equipment. It is recommended that this product is processed using a shallow screw, cross channel obstruction such as mixing rings should be avoided. Metering screw with 2.5-3:1 compression ratio in 20/1 extruders should produce satisfactory results. The compound supplied is in the cleanest state and is of the highest quality; however, the use of a breaker plate with a screen pack of approximately 20/40 or 20/60 mesh is recommended for optimal rheological flow and steady back pressure.
Pre-drying of the compound is not necessary, provided that the compound has been stored unopened in a cool, dry area.
The following conditions are given as a guide for processing (single extrusion):Temperature Profile:
°F
°C
Screw:
170-180
77-82
Zone 1 (feed):
210-220
99-105
Zone 2:
210-220
99-105
Zone 3:
210-220
99-105
Zone 4:
210-220
99-105
Head:
210-220
99-105
Die:
220-230
105-110
Packaging & Availability
- Packaging Type
- Packaging
- 1,750 pounds (794 Kg) per box.
Storage & Handling
- Storage
- SUPEROHM® 2575 containers should be stored at temperatures below 50 °C (120°F ) in a dry area to avoid massing of pellets. Product is recommended to be used within 12 Months.
- Handling
- To ensure health and safety, Material Safety Data Sheets (MSDS) are available and should be consulted prior to use.