Properties
- Mechanical Properties
- Thermal Properties
- Typical Properties
- Electrical Properties
- Processing Information (Injection Molding)
- Rheological Properties
| Value | Units | Test Method / Conditions | |
| Yield Stress (at 50mm/min) | 45.0 | MPa | ISO 527-1,-2 |
| Tensile Strain at Break (at 50mm/min) | min. 15 | % | Acc. ISO 527-1,-2 |
| Tensile Modulus (at 1mm/min) | 2400.0 | MPa | ISO 527-1,-2 |
| Flexural Strength (at 2 mm/min) | 70.0 | MPa | ISO 178 |
| Flexural Modulus (at 2 mm/min) | 2400.0 | MPa | ISO 178 |
| Izod Notched Impact Strength (at 23°C) | 21.0 | kJ/m² | ISO 180-1A |
| Izod Notched Impact Strength (at -30°C) | 12.0 | kJ/m² | ISO 180-1A |
| Yield Strain (at 50mm/min) | 2.6 | % | ISO 527-1,-2 |
| Charpy Impact Strength (at 23°C) | 130.0 | kJ/m² | ISO 179-1eU |
| Charpy Impact Strength (at -30°C) | 100.0 | kJ/m² | ISO 179-1eU |
| Charpy Notched Impact Strength (at 23°C) | 20.0 | kJ/m² | ISO 179-1eA |
| Charpy Notched Impact Strength (at -30°C) | 11.0 | kJ/m² | ISO 179-1eA |
| Ball Indentation Hardness | 102.0 | N/mm² | ISO 2039-1 |
| Value | Units | Test Method / Conditions | |
| Temperature of Deflection Under Load (at 1.80 MPa) | 98.0 | °C | ISO 75-1,-2 |
| Temperature of Deflection Under Load (at 0.45 MPa) | 102.0 | °C | ISO 75-1,-2 |
| Vicat Softening Temperature (at 50N, 120ºC/h) | 104.0 | °C | ISO 306 |
| Vicat Softening Temperature (at 50N, 50ºC/h) | 102.0 | °C | ISO 306 |
| Coefficient of Linear Thermal Expansion (Parallel, 23 - 55°C) | 0.8 | 10^{-4} /K | ISO 11359-1,-2 |
| Burning Rate (US-FMVSS, 2.0 mm) | 60.0 | mm/min | ISO 3795 |
| Glow Wire Test (GWFI, 2.0 mm) | 700.0 | °C | IEC 60695-2-12 |
| Value | Units | Test Method / Conditions | |
| Density | 1.04 | g/cm³ | ISO 1183 |
| Value | Units | Test Method / Conditions | |
| Relative Permittivity (at 100MHz) | 3.0 | — | IEC 60250 |
| Relative Permittivity (at 1MHz) | 2.9 | — | IEC 60250 |
| Dissipation Factor (at 100 MHz) | 50.0 | 10^{-4} | IEC 60250 |
| Dissipation Factor (at 1 MHz) | 90.0 | 10^{-4} | IEC 60250 |
| Volume Resistivity | 1.0e+16 | Ohm·m | IEC 60093 |
| Surface Resistivity | 1.0e+16 | Ohm | IEC 60093 |
| Electric Strength | 31.0 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index (Solution A) | 600.0 | Rating | IEC 60112 |
| Value | Units | Test Method / Conditions | |
| Injection Molding-Melt Temperature | 240.0 | ºC | ISO 294 |
| Injection Molding-Mold Temperature | 70.0 | ºC | ISO 294 |
| Injection Molding-Injection Velocity | 240.0 | mm/s | ISO 294 |
| Value | Units | Test Method / Conditions | |
| Molding Shrinkage (Normal, 60x60x2) | 0.5 - 0.7 | % | ISO 294-4 |
| Melt Volume-Flow Rate (at 220°C, 10kg) | 9.0 | cm³/(10 min) | ISO 1133 |
| Molding Shrinkage (Parallel, 60x60x2) | 0.5 - 0.7 | % | ISO 294-4 |