Elix - ABS E-LOOP H801 MR - ELIX Polymers - PC/ABS Alloy

Identification & Functionality

Polymer Name: PC/ABS Alloy
Plastics & Elastomers Functions: Resin
Technologies: Plastics
Product Families: Plastics — Engineering & Specialty Polymers
Blends & Alloys
Chemical Composition: Thermoplastic polymer blend of acrylonitrile-butadiene-styrene (ABS), polycarbonate (PC) modified.

Features & Benefits

Labeling Claims: Low Carbon Footprint (PCF),
Recycled
Materials Features: Heat Resistance,
High Flow,
Low Emissions
Major Benefits: Recycled material used in the formulation

Reduced carbon footprint

Equivalent properties to prime version

High heat resistance

Low emission grade

Applications & Uses

Markets: Automotive & Transportation,
Electrical & Electronics,
Industrial
Applications: Automotive & Transportation — Automotive
Electrical & Electronic Systems,
Exterior & Body
Industrial — Chemical & Industrial Manufacturing
Equipment & Parts
Electrical & Electronics — Parts & Components
Housings & Enclosures
Plastics & Elastomers End Uses: Automotive Grill,
Housings,
Industrial Applications,
Instrument Panel Parts,
Radiator Grill,
Tailgate Cover
Plastics & Elastomers Processing Methods: Injection Molding

Properties

	Value	Units	Test Method / Conditions
Yield Stress (50 mm/min, 23ºC, 50% H.R.)	47.0	MPa	ISO 527-1,2
Yield Strain (50 mm/min, 23ºC, 50% H.R.)	3.2	%	ISO 527-1, -2
Tensile Strain (at break, 50 mm/min, 23ºC, 50% H.R.)	min. 15	%	acc. ISO 527-1,2
Tensile Modulus (1 mm/min, 23ºC, 50% H.R.)	2400.0	MPa	ISO 527-1,2
Flexural Modulus (2 mm/min, 23ºC, 50% H.R.)	2350.0	MPa	ISO 178
Flexural Strength (2 mm/min, 23ºC, 50% H.R.)	78.0	MPa	ISO 178
Izod Notched Impact Strength (at 23ºC, 50% H.R.)	30.0	kJ/m²	ISO 180-1A
Izod Notched Impact Strength (at -30ºC, 50% H.R.)	13.0	kJ/m²	ISO 180-1A
Izod Notched Impact Strength (at 23ºC, 50% H.R., 3.2mm)	405.0	J/m	ASTM D 256
Izod Notched Impact Strength (at 23ºC, 50% H.R., 6.4mm)	280.0	J/m	ASTM D 256
Izod Notched Impact Strength (at -30ºC, 50% H.R., 3.2mm)	200.0	J/m	ASTM D 256
Charpy Impact Strength (at 23ºC, 50% H.R.)	230.0	kJ/m²	ISO 179-1eU
Charpy Impact Strength (at -30ºC, 50% H.R.)	160.0	kJ/m²	ISO 179-1eU
Charpy Notched Impact Strength (at 23ºC, 50% H.R.)	30.0	kJ/m²	ISO 179-1eA
Charpy Notched Impact Strength (at -30ºC, 50% H.R.)	18.0	kJ/m²	ISO 179-1eA
Ball Indentation Hardness (at 23ºC, 50% H.R.)	110.0	N/mm²	ISO 2039-1

	Value	Units	Test Method / Conditions
Vicat Softening Temperature (B50; 50ºC/h)	105.0	ºC	ISO 306
Vicat Softening Temperature (50N; 50ºC/h)	221.0	ºF	ASTM D 1525
Deflection Temperature (under load 1.80 MPa)	100.0	ºC	ISO 75-1,2
Deflection Temperature (under load 0.45 MPa)	107.0	ºC	ISO 75-1,2
Coefficient of Linear Thermal Expansion (Parallel, 23 to 55ºC)	0.85	10⁻⁴/K	ISO 11359 -1,2
Burning Behavior (1.6mm) UL 94	HB	Class	UL 94
Burning Rate (US-FMVSS)	40.0	mm/min	ISO 3795

	Value	Units	Test Method / Conditions
Density (at 25ºC)	1.07	g/cm³	ISO 1183-1

	Value	Units	Test Method / Conditions
Melt Temperature (for test specimens)	240.0	ºC	ISO 294
Mold Temperature (for test specimens)	70.0	ºC	ISO 294
Injection Velocity (for test specimens)	240.0	mm/s	ISO 294

	Value	Units	Test Method / Conditions
Melt Volume-Flow Rate (220ºC, 10kg)	11.0	cm³/10min	ISO 1133
Melt Flow Rate (230ºC, 3.8kg)	6.0	g/10min	ASTM D1238
Molding Shrinkage, Parallel (60x60x2 mm)	0.5-0.7	%	ISO 294-4
Molding Shrinkage, Normal (60x60x2 mm)	0.5-0.7	%	ISO 294-4

Regulatory & Compliance

Elix™ ABS E-LOOP H801 MR