Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
Applications & Uses
- Markets
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Electrical Properties
- Processing Information (Injection Molding)
Value | Units | Test Method / Conditions | |
Tensile Modulus (23°C/50% Relative Humidity, 5 mm/min) | 334000 | psi | ASTM D 638 |
Tensile Modulus (23°C/50% Relative Humidity, 1 mm/min) | 2300 | MPa | ISO 527-1,2 |
Yield Stress (23°C/50% Relative Humidity, 5 mm/min) | 38 | MPa | ASTM D 638 |
Yield Stress (23°C/50% Relative Humidity, 50 mm/min) | 41 | MPa | ISO 527-1,2 |
Flexural Strength (23°C/50% Relative Humidity, 2 mm/min) | 65 | MPa | ISO 178 |
Flexural Modulus (23°C/50% Relative Humidity, 1.3 mm/min) | 319000 | psi | ASTM D 790 |
Flexural Modulus (23°C/50% Relative Humidity, 2 mm/min) | 2200 | MPa | ISO 178 |
Charpy Notched Impact Strength (23°C (73°F), 50% Relative Humidity) | 18 | kJ/m2 | ISO 179-1eA |
Charpy Notched Impact Strength (-30°C (-22°F), 50% Relative Humidity) | 11 | kJ/m2 | ISO 179-1eA |
Charpy Impact Strength (23°C (73°F), 50% Relative Humidity) | 100 | kJ/m2 | ISO 179-1eU |
Charpy Impact Strength (-30°C (-22°F), 50% Relative Humidity) | 80 | kJ/m2 | ISO 179-1eU |
Izod Notched Impact Strength (-22°F (-30°C), 50% Relative Humidity, 3.2mm, 1/8”) | 125 | J/m | ASTM D 256 |
Izod Notched Impact Strength (73°F (23°C), 50% Relative Humidity, 3.2mm, 1/8”) | 235 | J/m | ASTM D 256 |
Izod Notched Impact Strength (73°F (23°C), 50% Relative Humidity, 6.4mm,1/4”) | 175 | J/m | ASTM D 256 |
Izod Notched Impact Strength (23°C (73°F), 50% Relative Humidity) | 18 | kJ/m2 | ISO 180-1A |
Izod Notched Impact Strength (-30°C (-22°F), 50% Relative Humidity) | 12 | kJ/m2 | ISO 180-1A |
Ball Indentation Hardness (23°C/50% Relative Humidity) | 103 | N/mm2 | ISO 2039-1 |
Value | Units | Test Method / Conditions | |
Melt Flow Rate - MFR (230°C, 3.8Kg) | 11 | g/10min | ASTM D1238 |
Melt Volume Flow Rate - MVFR (220°C, 10Kg) | 32 | cm3/10min | ISO 1133 |
Molding Shrinkage - Normal (60X60X2 mm) | 0.6 | % | ISO 294-4 |
Molding Shrinkage - Parallel (60X60X2 mm) | 0.6 | % | ISO 294-4 |
Density (25°C) | 1.05 | g/cm3 | ISO 1183-1 |
Value | Units | Test Method / Conditions | |
Coefficient Of Linear Thermal Expansion - Parallel (23 to 55°C) | 1 | 10-4/K | ISO 11359 -1,2 |
Coefficient Of Linear Thermal Expansion - Transverse (23 to 55°C) | 1 | 10-4/K | ISO 11359 -1,2 |
Deflection Temperature Under Load (0.45 Mpa) | 97 | °C | ISO 75-1,2 |
Deflection Temperature Under Load (1.80 Mpa) | 92 | °C | ISO 75-1,2 |
Vicat Softening Temperature (50N, 50°C/h) | 203 | ºF | ASTM D 1525 |
Vicat Softening Temperature (B120, 120°C/h) | 97 | °C | ISO 306 |
Vicat Softening Temperature (B50, 50°C/h) | 95 | °C | ISO 306 |
Value | Units | Test Method / Conditions | |
Relative Permittivity (23°C/50 % Relative Humidity, 1 MHz) | 2.9 | - | IEC 60250 |
Relative Permittivity (23°C/50 % Relative Humidity, 100 Hz) | 2.9 | — | IEC 60250 |
Dissipation Factor (23°C/50 % Relative Humidity, 100 Hz) | 73 | 10-4 | IEC 60250 |
Volume Resistivity (23°C/50 % Relative Humidity) | 1E16 | Ohm·m | IEC 60093 |
Surface Resistivity (23°C/50 % Relative Humidity) | 1E16 | Ohm | IEC 60093 |
Electric Strength (23°C/50 % Relative Humidity, 1 mm) | 35 | kV/mm | IEC 60243-1 |
Value | Units | Test Method / Conditions | |
Mold Temperature | 80 | °C | — |
Injection Velocity | 240 | mm/s | ISO 294 |
Melt Temperature | 240 | °C | ISO 294 |
Packaging & Availability
- Regional Availability