Properties
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Processing Information (Injection Molding)
| Value | Units | Test Method / Conditions | |
| Tensile Strength at Yield | 60 | MPa | ASTM D 638 |
| Tensile Elongation at Break | 50 | % | ASTM D638 |
| Flexural Strength | 90 | MPa | ASTM D 790 |
| Flexural Modulus | 2703 | MPa | ASTM D 790 |
| Izod Notched Impact Strength (73°F) | 160 | J/m | ASTM D256 |
| Value | Units | Test Method / Conditions | |
| Melt Flow Rate - MFR (250°C/2.16 kg) | 28 | g/10min | ASTM D1238 |
| Molding Shrinkage - Flow (0.126 in (3.20 mm)) | 0.406 - 0.508 | mm/mm | ASTM D955 |
| Specific Gravity | 1.3 | - | STANDARD D 792 |
| Value | Units | Test Method / Conditions | |
| Heat Deflection Temperature - HDT (264 psi) | 135 | °F | ISO 75-93 |
| Heat Deflection Temperature - HDT (66 psi) | 195 | °C | ASTM D648 |
| Value | Units | Test Method / Conditions | |
| Drying Temperature | 250 | °F | — |
| Drying Time | 3.0 - 4.0 | h | — |
| Maximum Drying Time | 8 | h | — |
| Suggested Maximum Moisture | 0.0002 | % | — |
| Rear Barrel Temperature | 410 - 440 | °F | — |
| Middle Barrel Temperatures | 430 - 470 | °F | — |
| Front Barrel Temperatures | 450 - 500 | °F | — |
| Nozzle Temperature | 460 - 500 | °F | — |
| Back Pressure | 145 - 290 | psi | — |
| Mold Temperature | 120 - 170 | °F | — |
| Screw Speed | 30 - 80 | rpm | — |
| Melt Temperature | 470 - 500 | °F | — |