Value | Units | Test Method / Conditions | |
Tensile Strength at Yield | 59 | MPa | ASTM D 638 |
Tensile Elongation at Break | 100 | % | ISO 527 |
Tensile Modulus | 2000 | MPa | ISO 527 |
Flexural Strength | 74 | MPa | ASTM D 790 |
Flexural Modulus | 2000 | MPa | ASTM D 790 |
Izod Notched Impact Strength (73°F) | 491 | J/m | ASTM D256 |
Value | Units | Test Method / Conditions | |
Melt Flow Rate - MFR (250°C/10 kg) | 28 | g/10min | ASTM D1238 |
Molding Shrinkage - Flow (0.126 in (3.20 mm)) | 0.127 - 0.152 | mm/mm | ASTM D955 |
Specific Gravity | 1.12 | - | ASTM D 792 |
Value | Units | Test Method / Conditions | |
Heat Deflection Temperature - HDT (264 psi) | 110 | °C | ASTM D648 |
Heat Deflection Temperature - HDT (66 psi) | 123 | °C | ASTM D648 |
Value | Units | Test Method / Conditions | |
Drying Temperature | 180 - 220 | °F | — |
Drying Time | 2.0 - 4.0 | h | — |
Maximum Drying Time | 4 | h | — |
Suggested Maximum Moisture | 0.0002 | % | — |
Rear Barrel Temperature | 450 - 500 | °F | — |
Middle Barrel Temperatures | 455 - 505 | °F | — |
Front Barrel Temperatures | 465 - 525 | °F | — |
Nozzle Temperature | 475 - 525 | °F | — |
Back Pressure | 25 - 100 | psi | — |
Mold Temperature | 175 - 200 | °F | — |
Screw Speed | 25 - 75 | rpm | — |
Melt Temperature | 475 - 525 | °F | — |