Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Fillers Included
- Polymer Name
- Technologies
- Product Families
Features & Benefits
- Materials Features
Applications & Uses
- Applications
- Plastics & Elastomers Processing Methods
Properties
- Color
- Mechanical Properties
- Thermal Properties
- Electrical Properties
- Other Properties
- Processing Information
Processing Parameter Value Unit Cylinder/processing temperature 260 - 295 °C Mold temperature 100 - 150 °C - This material can be processed as a thermoplastic taking the normal technical provisions into account. The above mentioned information refers exclusively to the injection molding process.
- Processing should be carried out as gently as possible, in order to maintain the maximum fiber length in the component. Back pressure and injection rate should be adjusted to the component geometry accordingly. The optimum processing temperature depends upon the respective geometry of the molded part and can be different from machine to machine.
- Predrying
Predrying Value Unit Drying temperature 80 °C Drying time 4 - 5 h - To achieve optimum mechanical properties, it is recommended to pre-dry the material w ith the above mentioned parameters.
| Value | Units | Test Method / Conditions | |
| Charpy Impact Strength (2,0 J) | 25 | kJ/m2 | DIN EN ISO 179-1eU |
| Elongation at Break (50 mm/min) | 1.5 | % | DIN EN ISO 527-1 |
| Modulus of Elasticity (Tensile test, 50 mm/min) | 13000 | MPa | DIN EN ISO 527-1 |
| Tensile Strength (50 mm/min) | 105 | MPa | DIN EN ISO 527-1 |
| Value | Units | Test Method / Conditions | |
| Glass Transition Temperature | 50 | °C | DIN 53765 |
| Heat Distortion Temperature (HDTA) | 252 | °C | ISO-R 75 Method A |
| Melting Temperature | 255 | °C | DIN 53765 |
| Service Temperature (long term) | 120 | °C | — |
| Service Temperature (short term) | 180 | °C | — |
| Specific Heat | 1.09 | J/(g*K) | DIN EN 821 |
| Thermal Conductivity (in-plane) | 3.5 | W/(K*m) | DIN EN 821 |
| Thermal Conductivity (through-plane) | 1.5 | W/(K*m) | DIN EN 821 |
| Thermal Diffusivity (longitudinal) | 1.6 | mm2/s | DIN EN 821 |
| Thermal Diffusivity (transverse) | 0.7 | mm2/s | DIN EN 821 |
| Thermal Expansion (CLTE) Longitudinal (at 23 - 45°C) | 25 | 10^-6 K^-1 | DIN EN ISO 11359-1;2 |
| Thermal Expansion (CLTE) Longitudinal (at 70 - 120°C) | 25 | 10^-6 K^-1 | DIN EN ISO 11359-1;2 |
| Thermal Expansion (CLTE) Transverse (at 23 - 45°C) | 50 | 10^-6 K^-1 | DIN EN ISO 11359-1;2 |
| Thermal Expansion (CLTE) Transverse (at 70 - 120°C) | 75 | 10^-6 K^-1 | DIN EN ISO 11359-1;2 |
| Value | Units | Test Method / Conditions | |
| Surface Resistivity | 5 x 10^12 | Ω | DIN EN 61340-2-3 |
| Volume Resistivity | 3.6 x 10^11 | Ω*m | DIN EN 61340-2-3 |
| Value | Units | Test Method / Conditions | |
| Bulk Density | 0.79 | g/cm3 | EN ISO 60 |
| Flammability (UL94) | HB | — | DIN IEC 60695-11-10 |
| Melt Flow Index (280°C / 5 kg) | 40 | g/10 min | DIN EN ISO 1133 |
| Molding Shrinkage (in-plane) | 0.36 | % | DIN EN ISO 294-4 |
| Molding Shrinkage (through-plane) | 0.67 | % | DIN EN ISO 294-4 |
| MVR (280°C / 5 kg) | 26.5 | cm3/10 min | DIN EN ISO 1133 |
| Water Absorption (23°C / 50% relative humidity up to saturation) | 1.3 | % | DIN EN ISO 62 |
Storage & Handling
- Storage & Shelf Life
- The granules must be stored in dry, normally tempered rooms and in closed containers. For moisture-sensitive materials, the granules must be sealed airtight. Protection against direct sunlight must be guaranteed. The granules are usually subject to the requirements of no shelf life limitation. Shelf Life maybe limited by some additives.