Eplamid 6 carbon fiber reinforced compounds are used in all sectors of industry, offering a good balance of thermal and mechanical properties
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Flammability
Value | Units | Test Method / Conditions | |
Unnotched izod impact (23°C) | 25 | kJ/m² | ISO 180/1U |
Flexural modulus (2mm/min) (23°C) | 7000 | MPa | ISO 178 |
Flexural strength (2mm/min) (23°C) | 210 | MPa | ISO 178 |
Tensile modulus (1mm/min) (23°C) | 8500 | MPa | ISO 527-2 |
Tensile strain at break (5mm/min) (23°C) | 2 | MPa | ISO 527-2 |
Tensile stress at break (5mm/min) (23°C) | 120 | MPa | ISO 527-2 |
Unnotched charpy impact (23°C) | 30 | kJ/m² | ISO 179/1eU |
Value | Units | Test Method / Conditions | |
Mold shrinkage- parallel/normal (3mm) | 0,5/0,8 | % | ISO 294-4 |
Ash content | 10 | % | ISO 3451-4 |
Density (23°C) | 1,17 | g/cm3 | ISO 1183 |
Determination of water content | 0,1 | % | ISO 1183 |
Value | Units | Test Method / Conditions | |
Temp. of deflection under load (1,80 MPa) | 190 | °C | ISO 75-2/A |
Melting point | 220 | °C | ISO 3146 |
Notched charpy impact (23°C) | 6 | kJ/m² | ISO 75-2/B |
Notched izod impact (23°C) | 5 | kJ/m² | ISO 180/1A |
Temp. of deflection under load (0,45 MPa) | 210 | °C | ISO 75-2/B |
Value | Units | Test Method / Conditions | |
Properties | HB | - | EN 60695-11-10 |