Value | Units | Test Method / Conditions | |
Tensile Stress at Break | 40 | MPa | ISO 527-2/50 |
Tensile Stress at Yield | 55 | MPa | ISO 527-2/1A/50 |
Tensile Strain at Break | 80 | % | ISO 527-1, -2 |
Flexural Modulus (2 mm/min) | 2100 | MPa | ISO 178 |
Flexural Stress | 77 | MPa | ISO 178 |
Charpy V - Notch Edge (-30°C, 80x10x4 Sp=62 mm) | 13 | kJ/m2 | ISO 179/1eA |
Charpy V - Notch Edge (23°C, 80x10x4 Sp=62 mm) | 17 | kJ/m2 | ISO 179/1eA |
Charpy Unnotch Edge (-30°C, 80x10x4 Sp=62 mm) | 85 | kJ/m2 | ISO 179/1eU |
Charpy Unnotch Edge (23°C, 80x10x4 Sp=62 mm) | min. 100 | kJ/m2 | ISO 179/1eU |
Izod Notched Impact Strength (80x10x4, - 30°C) | 13 | kJ/m2 | ISO 180/1A |
Izod Notched Impact Strength (80x10x4, 23°C) | 15 | kJ/m2 | ISO 180/1A |
Izod Unnotched Impact Strength (80x10x4, - 30°C) | 75 | kJ/m2 | ISO 180/1U |
Izod Unnotched Impact Strength (80x10x4, 23°C) | min. 100 | kJ/m² | ISO 180/1U |
Value | Units | Test Method / Conditions | |
Mold Shrinkage - Flow (4mm) | 1.4 - 1.6 | % | E2P Method |
Density | 1.1 | g/cm3 | ISO 1183 |
Value | Units | Test Method / Conditions | |
HDT/Ae (1.8 MPa Edge 120x10x4 Sp=100mm) | 64 | °C | ISO 75/Ae |
Value | Units | Test Method / Conditions | |
Drying Temperature | 75 - 85 | °C | - |
Mold Temperature | 60 - 90 | °C | -- |
Drying Time | 4.0 - 6 | hrs | - |
Front - Zone 3 Temperature | 240 - 250 | °C | - |
Maximum Moisture Content | 0.2 | % | - |
Melt Temperature | 240 - 250 | °C | - |
Middle - Zone 2 Temperature | 230 - 240 | °C | - |
Rear - Zone 1 Temperature | 220 - 230 | °C | - |