Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Applications & Uses
- Plastics & Elastomers Processing Methods
Properties
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Processing Parameters
Value | Units | Test Method / Conditions | |
Tensile Modulus (1 mm/min) | 4300 | MPa | ISO 527 |
Tensile Stress at Break | 65 | MPa | ISO 527-2 |
Tensile Strain at Break | 5 | - | ISO 527-2 |
Flexural Modulus | 3300 | MPa | ASTM D 790 |
Flexural Stress | 100 | MPa | ISO 178 |
Charpy V - Notch Edge (23°C, 80x10x4 Sp=62 mm) | 4 | kJ/m2 | ISO 179/1eA |
Charpy Unnotch Edge (23°C, 80x10x4 Sp=62 mm) | 25 | kJ/m2 | ISO 179/1eU |
Izod Notched Impact Strength (80x10x4, 23°C) | 4.5 | kJ/m2 | ISO 180/1A |
Izod Unnotched Impact Strength (80x10x4, 23°C) | 25 | kJ/m2 | ISO 180/1U |
Value | Units | Test Method / Conditions | |
Mold Shrinkage - Flow (4mm) | 1.1 to 1.3 | % | E2P Method |
Density | 1.29 | g/cm3 | ISO 1183 |
Value | Units | Test Method / Conditions | |
HDT/Af (1.8 MPa Flatw 80x10x4 Sp=64mm) | 70 | °C | ISO 75/Af |
Value | Units | Test Method / Conditions | |
Drying Temperature | 75 - 85 | °C | - |
Mold Temperature | 60 - 90 | °C | -- |
Drying Time | 4.0 - 6 | hrs | - |
Front - Zone 3 Temperature | 270 - 290 | °C | - |
Maximum Moisture Content | 0.2 | % | - |
Melt Temperature | 270 - 290 | °C | - |
Middle - Zone 2 Temperature | 270 - 280 | °C | - |
Rear - Zone 1 Temperature | 260 - 280 | °C | - |