Value | Units | Test Method / Conditions | |
Tensile Modulus (1 mm/min) | 4500 | MPa | ISO 527 |
Tensile Stress at Break (5 mm/min) | 80 | MPa | ISO 527-2/1A |
Tensile Strain at Break (5 mm/min) | 9 | % | ISO 527 |
Flexural Modulus (2 mm/min) | 4400 | MPa | ISO 178 |
Flexural Stress at Break (2 mm/min) | 130 | MPa | ISO 178 |
Charpy Unnotch Edge (23°C, 80x10x4 Sp=62 mm) | 30 | kJ/m2 | ISO 179/1eU |
Izod Notched Impact Strength (80x10x4, - 20°C) | 3 | kJ/m2 | ISO 180/1A |
Izod Notched Impact Strength (80x10x4, - 40°C) | 2 | kJ/m2 | ISO 180/1A |
Izod Notched Impact Strength (80x10x4, 23°C) | 4 | kJ/m2 | ISO 180/1A |
Value | Units | Test Method / Conditions | |
Mold Shrinkage on Tensile Bar - Flow | 1.1 - 1.5 | % | E2P Method |
Water Absorption (23°C/Sat) | 5.5 | % | ISO 62 |
Density | 1.37 | g/cm3 | STANDARD ISO 1183 |
Value | Units | Test Method / Conditions | |
HDT/Ae (1.8 MPa Edge 120x10x4 Sp=100mm) | 100 | °C | ISO 75/Ae |
HDT/Be (0.45MPa Edge 120x10x4 Sp=100mm) | 235 | °C | ISO 75/Be |
Coefficient of Thermal Expansion - Flow (23°C to 60°C) | 4.0e-05 | 1/°C | ISO 11359-2 |
Coefficient of Thermal Expansion - Xflow (23°C to 60°C) | 4.0e-05 | 1/°C | ISO 11359-2 |
Vicat Softening Temperature (Rate A/50) | 253 | °C | ISO 306 |
Value | Units | Test Method / Conditions | |
Comparative Tracking Index - CTI | 500 | V | UL 746 |
Value | Units | Test Method / Conditions | |
Oxygen Index - LOI | 26 | % | ISO 4589 |
Ul E2P Measurement, 94HB Flame Class Rating | 1.6 | mm | UL 94 |
Value | Units | Test Method / Conditions | |
Drying Temperature | 75 - 85 | °C | - |
Drying Time | 4.0 - 6 | hrs | - |
Front - Zone 3 Temperature | 260 - 290 | °C | - |
Maximum Moisture Content | 0.2 | % | - |
Melt Temperature | 2670 - 290 | °C | - |
Middle - Zone 2 Temperature | 260 - 280 | °C | - |
Mold Temperature | 70 - 120 | °C | - |
Rear - Zone 1 Temperature | 270 - 290 | °C | - |