Value | Units | Test Method / Conditions | |
Tensile Modulus (1 mm/min) | 7000 | MPa | ISO 527 |
Tensile Stress at Break (50 mm/min) | 128 | MPa | ISO 527 |
Tensile Strain at Break (50 mm/min) | 2.6 | % | ISO 527-1,-2 |
Flexural Modulus (2 mm/min) | 6000 | MPa | ISO 178 |
Flexural Stress at Break (2 mm/min) | 185 | MPa | ISO 178 |
Charpy V - Notch Edge (23°C, 80x10x4 Sp=62 mm) | 5.7 | kJ/m2 | ISO 179/1eA |
Charpy Unnotch Edge (23°C, 80x10x4 Sp=62 mm) | 46 | kJ/m2 | ISO 179/1eU |
Izod Notched Impact Strength (80x10x4, 23°C) | 6 | kJ/m2 | ISO 180/1A |
Izod Unnotched Impact Strength (80x10x4, 23°C) | 42 | kJ/m2 | ISO 180/1U |
Value | Units | Test Method / Conditions | |
Mold Shrinkage - Flow (4mm) | 0.2 - 0.4 | % | E2P Method |
Density | 1.36 | g/cm3 | ISO 1183/A |
Value | Units | Test Method / Conditions | |
Melting Point - DSC | 264 | °C | ISO 3146 |
Heat Deflection Temperature - HDT (1.82 MPa, 3.2mm, Unannealed) | 230 | °C | ASTM D 648 |
Value | Units | Test Method / Conditions | |
Mold Temperature | 70 - 90 | °C | -- |
Drying Temperature | 70 - 80 | °C | - |
Drying Time | 4.0 - 6 | hrs | - |
Front - Zone 3 Temperature | 265 - 280 | °C | - |
Maximum Moisture Content | 0.2 | % | - |
Melt Temperature | 265 - 280 | °C | - |
Middle - Zone 2 Temperature | 270 - 285 | °C | - |
Rear - Zone 1 Temperature | 260 - 280 | °C | - |