Starflam™ RF0068E

Identification & Functionality

Additives Included

Flame Retardant

Chemical Family

Polyamides

Fillers Included

Glass Fiber

Polymer Name

Polyamide 66 (PA 66)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Engineering & Specialty Polymers

Polyamides

Features & Benefits

Labeling Claims

Halogen-free

Materials Features

Flame Retardant

Applications & Uses

Plastics & Elastomers Processing Methods

Injection Molding

Properties

Flame Rating

UL 94 V0

Flame Rating

UL 94 V0

Mechanical Properties

	Value	Units	Test Method / Conditions
Tensile Stress at Break	130	MPa	ISO 527-2/1A/5
Tensile Strain at Break	2.4	%	ASTM D 638
Flexural Modulus (2 mm/min)	8000	MPa	ISO 178
Flexural Stress at Yield (2 mm/min)	180	MPa	ISO 178
Izod Notched Impact Strength (80x10x4, 23°C)	7	kJ/m2	ISO 180/1A
Izod Unnotched Impact Strength (80x10x4, 23°C)	40	kJ/m2	ISO 180/1U

Physical Properties

	Value	Units	Test Method / Conditions
Mold Shrinkage - Flow (24 h)	0.2 - 0.5	%	ISO 294
Water Absorption (23°C/24 h)	0.2	%	ISO 62-1
Density	1.42	g/cm3	STANDARD ISO 1183

Thermal Properties

	Value	Units	Test Method / Conditions
HDT/Af (1.8 MPa Flatw 80x10x4 Sp=64mm)	225	°C	ISO 75/Af
Relative Temperature Index - Electrical	140	°C	UL 746B
Relative Temperature Index - Mechanical With Impact	105	°C	UL 746B
Relative Temperature Index - Mechanical Without Impact	140	°C	UL 746B

Electrical Properties

	Value	Units	Test Method / Conditions
Comparative Tracking Index - CTI	600	V	UL 746
High Ampere Arc Ign (Surface, PLC)	0	-	UL 746A

Flammability

	Value	Units	Test Method / Conditions
Glow Wire Flammability Index - GWFI (Passes at 960°C)	0.8	mm	IEC 60695-2-12
Glow Wire Ignitability Temperature - GWIT (1.0 mm)	725	°C	IEC 60695-2-13
Glow Wire Ignitability Temperature - GWIT (3.0 mm)	750	°C	IEC 60695-2-13
Ul Recognized, 94V - 0 Flame Class Rating	0.8	mm	UL 94

Processing Parameters

	Value	Units	Test Method / Conditions
Drying Temperature	80	°C	—
Mold Temperature	60 - 100	°C	--
Drying Time	4	hrs	—
Front - Zone 3 Temperature	270 - 280	°C	—
Maximum Moisture Content	0.15 - 0.25	%	—
Melt Temperature	270 - 280	°C	—
Middle - Zone 2 Temperature	270 - 280	°C	—
Rear - Zone 1 Temperature	265 - 275	°C	—

Regulatory & Compliance

Certifications & Compliance

UL 94