Value | Units | Test Method / Conditions | |
Tensile Modulus (1 mm/min) | 9400 | MPa | ISO 527 |
Tensile Stress at Yield | 110 | MPa | ISO 527 |
Tensile Strain at Break | 1.7 | % | ASTM D 638 |
Flexural Modulus | 6700 | MPa | ASTM D 790 |
Flexural Stress | 125 | MPa | ISO 178 |
Izod Notched Impact Strength (80x10x4, 23°C) | 8.4 | kJ/m2 | ISO 180/1A |
Izod Unnotched Impact Strength (80x10x4, 23°C) | 32 | kJ/m2 | ISO 180/1U |
Value | Units | Test Method / Conditions | |
Mold Shrinkage - Flow (24 h) | 0.3 - 0.5 | % | ISO 294 |
Density | 1.51 | g/cm3 | ISO 1183 |
Value | Units | Test Method / Conditions | |
Melting Point - DSC | 223 | °C | ISO 3146 |
HDT/Af (1.8 MPa Flatw 80x10x4 Sp=64mm) | 193 | °C | ISO 75/Af |
Value | Units | Test Method / Conditions | |
Drying Temperature | 70 - 80 | °C | — |
Drying Time | 2.0 - 4 | hrs | — |
Front - Zone 3 Temperature | 225 - 235 | °C | — |
Maximum Moisture Content | 0.1 | % | — |
Melt Temperature | 225 - 235 | °C | — |
Middle - Zone 2 Temperature | 225 - 235 | °C | — |
Mold Temperature | 70 - 80 | °C | — |
Rear - Zone 1 Temperature | 225 - 235 | °C | — |