Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
Applications & Uses
Properties
- Color
- Flame Rating
- Flame Rating
- IEC 60695-11-10 HB
- Mechanical Properties
- Physical Properties
- Typical Properties
- Thermal Properties
- Other Properties
- Processing Parameters
- Electrical Properties and Flammability
| Value | Units | Test Method / Conditions | |
| Flexural Modulus (at 23°C) | 8250 | MPa | ISO 527 |
| Stress at break | 175 | MPa | ISO 527 |
| Izod Impact Notched (at -30°C) | 12 | kJ/m2 | ISO 180/1A |
| Tensile Modulus | 9500 | MPa | ISO 527-2/1A/1 |
| Izod Impact Notched (at 23°C) | 16 | kJ/m2 | ISO 180/1A |
| Izod Impact Un Notched (-30°C) | 80 | kJ/m2 | ISO 180/1U |
| Strain at break | 3.5 | % | ISO 527 |
| Izod Impact Un Notched (at 23°C) | 95 | kJ/m2 | ISO 180/1U |
| Strain at Break (at 23 °C) | 3.5 | % | ISO 527 |
| Stress at Break (at 23 °C) | 175 | MPa | ISO 527 |
| Tensile Modulus (at 23°C) | 9500 | MPa | ISO 527 |
| Izod notched impact strength, +23° | 16 | kJ/m2 | ISO 180/1A |
| Izod notched impact strength | 12 | kJ/m2 | ISO 180/1A |
| Izod impact strength, +23° | 95 | kJ/m2 | ISO 180/1U |
| Temperature | -30 | °C | — |
| Value | Units | Test Method / Conditions | |
| Density | 1360 | kg/m3 | ISO 1183 |
| Value | Units | Test Method / Conditions | |
| Density | 1.36 | g/cm3 | ISO 1183 |
| Moisture Absorption (50% RH at 23°C) | 2.1 | % | ISO 62 |
| Moisture Content | max. 0.2 | % | ISO 960 |
| Molding Shrinkage (Normal) | 1 | % | Eurotec |
| Molding Shrinkage (Parallel) | 0.2 | % | Eurotec |
| Value | Units | Test Method / Conditions | |
| Heat Deformation Temperature (0.45 MPa) | 220 | °C | ISO 75 |
| Temperature of deflection under load (0.45 Mpa) | 220 | °C | ISO 75-1/-2 |
| Temperature of deflection under load (1.80 Mpa) | 210 | °C | ISO 75-1/-2 |
| Heat Deformation Temperature (1.80 MPa) | 210 | °C | ISO 75 |
| Melting Temperature (10 K/min) | 223 | °C | ISO 11357 |
| Vicat Softening Temperature (50N) | 215 | °C | ISO 306 |
| Melting temperature (10°C/min) | 223 | °C | ISO 11357-1/-3 |
| Thickness tested | 0.8 | mm | — |
| Vicat softening temperature | 215 | °C | ISO 306 |
| Burning Behavior at 1.5 mm nominal thickness | HB | class | IEC 60695-11-10 |
| Burning Behavior at thickness | HB | class | IEC 60695-11-10 |
| Value | Units | Test Method / Conditions | |
| Humidity absorption | 2.1 | % | Sim. to ISO 62 |
| Moisture Content | 0.2 | % | — |
| Value | Units | Test Method / Conditions | |
| Back Pressure | Low | — | — |
| Drying | 80 / 2 - 4 | °C / hr | — |
| Feed Throat Temperature | 60 - 80 | °C | — |
| Hold Pressure | 50 - 100 | MPa | — |
| Injection Speed | Fast | — | — |
| Mold Temperature | 70 - 110 | °C | — |
| Processing Temperature | 270 - 300 | °C | — |
| Value | Units | Test Method / Conditions | |
| Flame Rating (0.75 mm) | HB | — | UL94 |
| Flame Rating (1.6 mm) | HB | — | UL94 |
| Surface Resistivity | 10000000000000 | Ohm | IEC 60093 |
| Volume Resistivity | 1E+15 | Ohm-cm | IEC 60093 |
Regulatory & Compliance