Products

Fiberglass (A/Asia) Sales Pty 268 BQTN Laminating Resin is a thixatropic, quick-curing unsaturated polyester resin of orthophthalic grade for general laminating purposes. It is pre-accelerated, and suitable for both hand lay-up and gun spray-up. It is available in Australia either as 268 BQTN LSE waxed, or 268BQTN unwaxed. This resin is used for making a variety of glass fiber reinforced plastic products such as boats and canoes, bus shelters, telephone booths, stadium seating, bath tubs, water and storage tanks, cooling towers, plant and flowers pots, bath units, models, containers, dust bins, safety helmets, water and oil pipes, ash trays, septic tanks, car body parts, sporting equipment, concrete framings, chairs and tables, and other household as well as industrial articles. Glass reinforced laminates made with this resin possess excellent mechanical strength along with good rigidity and outstanding durability. The SHCP 268BQT resin and its variants are approved by Lloyd’s Register of Shipping for boat construction.

Fiberglass (A/Asia) Sales Pty 342S VE Resin is a general purpose type resin used in the manufacture of fiberglass reinforced plastic components, and other applications where it is resistant to a broad range of acid base and salt solutions up to 100 Deg. C. 342S Vinyl Ester Resin is normally supplied thixotropic and promoted to be catalyzed by either Interox SR or Butanox M50 catalysts. Other MEKP catalysts should be first tested before used for the development of a satisfactory level of cure. Where exposure to severe corrosive environments is to be encountered, post curing of laminates is strongly recommended.

Fiberglass (A/Asia) Sales Pty 901 Swancor VE Resin is a general purpose type resin used in the manufacture of fiberglass reinforced plastic components, and other applications where it is resistant to a broad range of acid base and salt solutions up to 100 Deg. C. Swancor 901 Vinyl Ester Resin is normally supplied thixotropic and promoted to be catalyzed by either Interox SR or Butanox M50 catalysts. Other MEKP catalysts should be first tested before used for the development of a satisfactory level of cure. Where exposure to severe corrosive environments is to be encountered, post curing of laminates is strongly recommended.

Fiberglass (A/Asia) Sales Pty 6060 LSE Resin is a promoted orthophthalic laminating resin exhibiting low styrene emission. This grade shows excellent glass fiber wet out and is designed for use in general spray depositing and hand lay up. Long green time, low exotherm and low color in thick sections make this resin ideal for large structures or multiple laminates. 6060 LSE contains an ingredient which reduces styrene emission during lamination and in the period prior to gelation. Low styrene emission resins alone will not enable the molder to comply with the recommended atmospheric styrene levels, but with appropriate ventilation, these resins may assist in reducing the level of styrene in the workshop to which workers are exposed. Tests carried out to TP 261.2 (Interlaminar adhesion) show no loss in adhesion after one day delayed lay-up.

Fiberglass (A/Asia) Sales Pty PVA Blue is a mold release agent intended for use on plugs and molds as an additional aid for release in conjunction with mold release waxes. Plastrene PVA No.5 Blue must not be applied to any surface that contains moisture or is sensitive to alcohol and water. The surface of the mold must be free of dust and should have been cleaned with mineral spirits or styrene to remove any traces of silicone based release agents. Plastrene PVA No.5 Blue may be applied by spray or hand application. For best results apply a mist coat first and then follow up with a heavier coat. The ultimate objective is to create a thin even film. Normal dry times are in the range of 15-30 minutes. The film should be dry to the touch before progressing.

Fiberglass (A/Asia) Sales Pty TGI Chopped Strand Mat is made of randomly, yet evenly distributed strands chopped from continuous “E” Glass fibers into 50mm lengths bonded with “emulsion binder”, possesses excellent surface bonding efficiency. It is suitable for use with most unsaturated polyester and vinyl ester resin systems in contact molding where fast wet-out and good molding performance is required. Taiwan Glass Industries Corporation Chopped Strand Mat has Lloyd’s Register of Shipping Approval, Garnisher Lloyd, Det Norske Veritas, and ISO 9002 approvals.