Fiberglass (A/Asia) Sales Pty 6060 LSE Resin

Fiberglass (A/Asia) Sales Pty 6060 LSE Resin is a promoted orthophthalic laminating resin exhibiting low styrene emission. This grade shows excellent glass fiber wet out and is designed for use in general spray depositing and hand lay up. Long green time, low exotherm and low color in thick sections make this resin ideal for large structures or multiple laminates. 6060 LSE contains an ingredient which reduces styrene emission during lamination and in the period prior to gelation. Low styrene emission resins alone will not enable the molder to comply with the recommended atmospheric styrene levels, but with appropriate ventilation, these resins may assist in reducing the level of styrene in the workshop to which workers are exposed. Tests carried out to TP 261.2 (Interlaminar adhesion) show no loss in adhesion after one day delayed lay-up.

Polymer Name: Thermoset (unspecified)

Chemical Family: Orthophthalics, Unsaturated Polyester (UPE)

Processing Methods: Hand Lay-up, Spray Lay-up

End Uses: Doors, FRP Boats

Technical Data Sheet
  • TypeDocument Name
View All Documents

Knowde Enhanced TDS

Identification & Functionality

Chemical Family

Orthophthalics,

Unsaturated Polyester (UPE)

Polymer Name

Thermoset (unspecified)

Composite Materials Functions

Resins, Binders & Matrix Materials

Technologies

Composite Materials

Product Families

Composite Materials — Polymers & Resins

Thermoset Resins

Applications & Uses

Markets

Automotive & Transportation,

Building & Construction

Applications

Building & Construction — Building Materials

Interior Fixtures

Automotive & Transportation — Transportation

Marine

Composites End Use

Doors,

FRP Boats

Composites Processing Methods

Hand Lay-up,

Spray Lay-up

Properties

Color

Blue

Physical Properties
ValueUnitsTest Method / Conditions
Barcol Hardness (GYZ 934-1)40.0—EN 59
Tensile strength56.0MPaISO R527
Tensile strength105.0MPaISO 3268
Tensile strength after immersion in boiling water for two hours43.0MPaISO R527
Flexural strength78.0MPaISO 178
Flexural strength after immersion in boiling water for two hours70.0MPaISO 178
Tensile Modulus4.0GPaISO R527
Tensile modulus after immersion in boiling water for two hours3.0GPaISO R527
Tensile modulus after immersion in boiling water for two hours7.0GPaISO 3268
Flexural modulus4.0GPaISO 178
Flexural modulus7.0GPaISO 178
Flexural modulus after immersion in boiling water for two hours3.0GPaISO 178
Flexural modulus after immersion in boiling water for two hours7.0GPaISO 3268
Elongation at break2.0%ISO R527
Heat deflection temperature (1.8MPa)58.0°CISO 75
Water absorption (One day)15.0mgISO 62
Water absorption (One day)22.0mgISO 62
Water absorption (Seven days)22.0mgISO 180
Water absorption (Seven days)35.0mgISO 62
Tensile Strength after immersion in boiling water for two hours100.0MPaISO 3268
Flexural Strength182.0MPaISO 178
Flexural Strength after immersion in boiling water for two hours175.0MPaISO 178
Tensile modulus9.0GPaISO 3268
Impact strength, Jmin. 13.5—ISO 180
Typical Liquid Resin Properties
ValueUnitsTest Method / Conditions
AppearanceOpaque Blue, Clean—TP 202.8
Viscosity (25°C, 5 RPM Spindle 3)min. 1800cpsTP 201.24
Viscosity (25°C, 50 RPM Spindle 3)700 - 1000cpsTP 201.24
Volatile Content40 - 43%TP 200.25
Styrene Emissionmax. 20g/m²TP 261.4

Storage & Handling

Stability

Stability in the dark below 25ºC - 6 months in sealed container.